Selective growth of silicon oxide or silicon nitride on silicon surfaces in the presence of silicon oxide

1. A method for selectively depositing a silicon-containing dielectric material on an exposed first surface of a substrate, the method comprising:

providing the substrate having the exposed first surface, and an exposed second surface;

exposing the substrate to an acyl chloride that reacts with the exposed second surface to selectively form blocking groups on the exposed second surface relative to the exposed first surface, the acyl chloride having a chemical structure of

 wherein R 1 is hydrogen or an alkyl group; and

after exposing the substrate to the acyl chloride, performing one or more cycles of thermal atomic layer deposition to deposit a silicon-containing dielectric material selectively on the exposed first surface, each cycle comprising:

exposing the substrate to a silicon-containing precursor selected to adsorb onto the exposed first surface of the substrate, and

exposing the substrate to a second reactant to form the silicon-containing dielectric material selectively on the exposed first surface of the substrate.

2. The method of claim 1 , wherein the silicon-containing dielectric material is silicon nitride.

3. The method of claim 2 , wherein the second reactant selected from the group consisting of ammonia and hydrazines having the chemical structure

wherein R 2 , R 3 , R 4 , and R 5 are each hydrogen or an alkyl group.

4. The method of claim 2 , wherein the silicon-containing precursor is selected from the group consisting of silicon halides and aminosilanes.

5. The method of claim 1 , wherein the silicon-containing dielectric material is silicon oxide.

6. The method of claim 5 , wherein the second reactant is a weak oxidant.

7. The method of claim 5 , wherein the second reactant is selected from the group consisting of water, hydrogen peroxide, and ozone.

8. The method of claim 1 , wherein the acyl chloride is acetyl chloride.

9. The method of claim 1 , further comprising, prior to providing the substrate, depositing silicon nitride to form an untreated silicon nitride surface; and exposing the untreated silicon nitride surface to a mixture of ammonia and hydrogen gas and igniting a plasma for a duration between about 1 second and about 10 seconds to form the exposed second surface comprising primary amine groups.

10. The method of claim 9 , wherein amount of ammonia in the mixture of ammonia and hydrogen is less than about 1% by volume.

11. The method of claim 1 , further comprising, prior to providing the substrate, depositing silicon nitride to form an untreated silicon nitride surface and exposing the untreated silicon nitride surface to a mixture of nitrogen and hydrogen gas and igniting a plasma for a duration between about 1 second and about 10 seconds to form the exposed second surface comprising primary amine groups.

12. The method of claim 11 , wherein amount of nitrogen in the mixture of nitrogen and hydrogen is less than about 1% by volume.

13. The method of claim 1 , wherein the exposed second surface comprises surface terminated primary amine groups of silicon nitride deposited by chemical vapor deposition at a deposition temperature greater than about 500° C.

14. A method for selectively depositing a metal-containing dielectric material on an exposed first surface of a substrate, the method comprising:

providing the substrate having the exposed first surface, and an exposed second surface;

exposing the substrate to an acyl chloride that reacts with the exposed second surface to selectively form blocking groups on the exposed second surface relative to the exposed first surface, the acyl chloride having a chemical structure of

 wherein R1 is hydrogen or an alkyl group; and

after exposing the substrate to the acyl chloride, performing one or more cycles of thermal atomic layer deposition to deposit a metal-containing dielectric material selectively on the exposed first surface, each cycle comprising:

exposing the substrate to a metal-containing precursor selected to adsorb onto the exposed first surface of the substrate, and

exposing the substrate to a second reactant to form the metal-containing dielectric material selectively on the exposed first surface of the substrate.

15. The method of claim 14 , wherein the metal-containing dielectric material is selected from the group consisting of zirconium oxide, titanium oxide, tin oxide, hafnium oxide, and titanium nitride.

16. The method of claim 14 , wherein the acyl chloride is acetyl chloride.

17. The method of claim 14 , further comprising, prior to providing the substrate, depositing silicon nitride to form an untreated silicon nitride surface; and exposing the untreated silicon nitride surface to a gas and igniting a plasma for a duration between about 1 second and about 10 seconds to form the exposed second surface comprising primary amine groups.

18. The method of claim 17 , wherein the gas is selected from the group consisting of ammonia, nitrogen, hydrogen, and combinations thereof.

19. The method of claim 14 , wherein the exposed second surface comprises surface terminated primary amine groups of silicon nitride deposited by chemical vapor deposition at a deposition temperature greater than about 500° C.

20. The method of claim 14 , wherein the exposed first surface comprises a material selected from the group consisting of polysilicon, amorphous silicon, metals, and silicon nitride having single secondary amine terminated groups, and the exposed second surface comprises a silicon-containing material having a surface terminated group selected from the group consisting of hydroxyl and primary amine.