Poly(meth)acrylic acid (salt)-based particulate absorbent
A low cost, a disposable diaper is provided that presents no difficulties in disposable diaper manufacture in humid climates, and that has a minimal amount of flowback, and rapid absorption time. A particulate water-absorbing agent is provided having as the principal component a poly (meth)acrylic acid (salt)-based water absorbing resin, wherein the water-absorbing agent has a particle size distribution of a weight average particle diameter of 300 to 500 μm, a blocking ratio after moisture absorption when left for one hour at 25° C. and 90% relative humidity of 20% or less, a surface tension of 60 mN/m or more, and a gel capillary absorption (GCA) of 28.0 g/g or more.
1. A particulate water-absorbing agent comprising a poly (meth)acrylic acid (salt)-based water-absorbing resin as a main component, wherein
the particulate water-absorbing agent has:
a weight average particle diameter (D50) of 300 to 500 μm,
a blocking ratio after moisture absorption when left for one hour at 25° C. and 90% relative humidity of 20% or less,
a surface tension of 60 mN/m or more, and
a gel capillary absorption (GCA) of 28.0 g/g or more.
2. The particulate water-absorbing agent according to claim 1 , wherein the particulate water-absorbing aunt is surface crosslinked.
3. The particulate water-absorbing agent according to claim 1 , wherein the particulate water-absorbing agent has a fluid retention capacity without pressure (CRC) of 28 g/g or more.
4. The particulate water-absorbing agent according to claim 1 , wherein the particulate water-absorbing agent has a fluid retention capacity under pressure (AAP) of 25 g/g or more.
5. The particulate water-absorbing agent according to claim 1 , wherein the particulate water-absorbing agent has a water absorption time by Vortex method of 40 seconds or less.
6. The particulate water-absorbing agent according to claim 1 , wherein the particulate water-absorbing agent has a surface tension of 65 mN/m or more.
7. The particulate water-absorbing agent according to claim 1 , wherein the particulate water-absorbing agent has a gel capillary absorption (GCA) of 30.0 g/g or more.
8. The particulate water-absorbing agent according to claim 1 , comprising water-insoluble inorganic fine particles.
9. The particulate water-absorbing agent according to claim 8 , wherein the water-insoluble inorganic fine particles content is from 0.01 to 1.0% V by weight per 100% by weight of the poly(meth)acrylic acid (salt)-based water-absorbing resin (solid content).
10. The particulate water-absorbing agent according to claim 8 , wherein the volume average particle diameter of the water-insoluble inorganic fine particles is from 0.01 to 3 μm.
11. The particulate water-absorbing agent according to claim 1 , comprising a chelating agent.
12. The particulate water-absorbing agent according to claim 11 , wherein the chelating agent content is from 0.001 to 1 part by weight per 100 parts by weight of the poly(meth)acrylic acid (salt)-based water-absorbing resin (solid content).
13. The particulate water-absorbing agent according to claim 11 , wherein the chelating agent is a compound selected from the group consisting of an organic phosphorus chelating agent and an amino carboxylic acid chelating agent.
14. The particulate water-absorbing agent according to claim 1 , wherein the shape of the water-absorbing agent is an irregularly-crushed shape or granules thereof.
15. An absorbent article formed by including the particulate water-absorbing agent according to claim 1 and a hydrophilic fiber.