Self-replenishing boundary lubrication in hydrogels using zwitterionic polymers
A self-replenishing biocompatible hydrogel having a zwitterionic polymer embedded throughout the matrix system to act as a lubricant and a surface modified with the same zwitterionic polymer. When surface material loss occurs in the hydrogel, such as a surface crack or a scratch, the damage propagates through the matrix rupturing the pockets of lubricant. The zwitterionic polymer is then drawn into the site due to the change in entropy at the surface and the positive and negative charge groups of the side chains fuse across the damage cite due to strong electrostatic attraction causing inter-chain association.
1. A hydrogel having self-replenishing lubrication, comprising:
a matrix formed from a hydrogel polymer; and
a plurality of sulfobetaine zwitterionic polymer molecules blended in the matrix.
2. The hydrogel of claim 1 , wherein the hydrogel polymer comprises poly(vinyl alcohol).
3. A hydrogel having self-replenishing lubrication, comprising:
a matrix formed from poly(vinyl alcohol);
a plurality of zwitterionic polymer molecules blended in the matrix, wherein the zwitterionic polymer molecules comprise poly[2-(Methacryloyloxy) ethyl]dimethyl-(3-sulfopropyl) ammonium hydroxide).
4. The hydrogel of claim 3 , wherein the hydrogel polymer comprises poly(vinyl alcohol) and an initiator grafted to a surface of the poly(vinyl alcohol).
5. The hydrogel of claim 4 , wherein the initiator is α-chlorophenylacetyl chloride.
6. The hydrogel of claim 5 , wherein the plurality of zwitterionic polymer molecules are polymerized from the α-chlorophenylacetyl chloride initiator.
7. The hydrogel of claim 4 , wherein the initiator is α-bromoisobutyryl bromide.
8. The hydrogel of claim 5 , wherein the plurality of zwitterionic polymer molecules are polymerized from the α-bromoisobutyryl bromide initiator.
9. The hydrogel of claim 1 , wherein the hydrogel has an average modulus of above one Megapascal.
10. A method of making a hydrogel having self-replenishing lubrication, comprising the steps of:
forming a plurality of zwitterionic polymer molecules comprising poly[2-(Methacryloyloxy) ethyl]dimethyl-(3-sulfopropyl) ammonium hydroxide);
blending the plurality of zwitterionic polymer molecules with a hydrogel polymer comprising poly(vinyl alcohol);
subjecting the blended zwitterionic polymer molecules and polymer to a predetermined number of freeze-thaw cycles to embed the zwitterionic polymer molecules in a matrix of the hydrogel polymer.
11. The hydrogel of claim 10 , wherein the hydrogel has an average modulus of above one Megapascal.
12. A method of making a hydrogel having self-replenishing lubrication, comprising the steps of:
grafting an initiator to a surface of a dry hydrogel polymer comprising poly(vinyl alcohol);
initiating polymerization of plurality of zwitterionic molecules comprising poly[2-(Methacryloyloxy) ethyl]dimethyl-(3-sulfopropyl) ammonium hydroxide) from the initiator of the surface of the dry hydrogel polymer.
13. The method of claim 12 , wherein the initiator comprises a-chlorophenylacetyl chloride.
14. The method of claim 13 , wherein the initiator comprises α-bromoisobutyryl bromide.
15. The method of claim 12 , wherein the step of grafting the initiator to the surface of the dry hydrogel is performed in the presence of tetrahydrofuran.
16. The method of claim 15 , wherein the step of initiating polymerization of plurality of zwitterionic molecules from the initiator of the surface of the dry hydrogen polymer is performed in the presence of triflureoethanol.