Two-step method for strengthening glass
A method of strengthening an alkali aluminoborosilicate glass. A compressive layer extending from a surface of the glass to a depth of layer is formed by exchanging larger metal cations for smaller metal cations present in the glass. In a second step, metal cations in the glass are exchanged for larger metal cations to a second depth in the glass that is less than the depth of layer and increase the compressive stress of the compressive layer. Formation of the compressive layer and replacement of cations with larger cations can be achieved by a two-step ion exchange process. An alkali aluminoborosilicate glass having a compressive layer and a crack indentation threshold of at least 3000 gf is also provided.
1. An alkali aluminoborosilicate glass comprising 5-20 mol % B 2 O 3 , 2-8.3 mol % Li 2 O, lithium cations, sodium cations, and potassium cations, wherein the glass has a surface having a compressive layer extending from the surface to a depth of layer and is enriched in potassium cations to a second depth that is less than the depth of layer, and wherein the surface of the glass has a crack initiation layer threshold of at least 6000 gf upon indentation with a Vickers indenter, and wherein the surface has compressive stress of at least 711 MPa, wherein the glass is a glass sheet having a thickness of up to 2 mm.
2. The glass of claim 1 , further comprising 50-70 mol % SiO 2 ; 5-15 mol % Al 2 O 3 ; 0-20 mol % Na 2 O; and 0-10 mol % K 2 O.
3. The glass of claim 1 , wherein the surface has a compressive stress depth of layer is at least about 50 μm.
4. The glass of claim 1 , wherein the depth of layer is in a range from about 70 μm up to about 290 μm.
5. The glass of claim 1 , wherein the second depth is in a range from about 5 μm up to about 20 μm.
6. The glass of claim 1 , wherein the alkali aluminoborosilicate glass further comprises at least one of: 0-10 mol % P 2 O 5 ; 0-5 mol % MgO; 0-1 mol % CeO 2 ; and 0-1 mol % SnO 2 .
7. The glass of claim 1 , glass has a crack initiation layer threshold of at least 8000 gf upon indentation with a Vickers indenter.
8. An alkali aluminoborosilicate glass comprising 50-70 mol % SiO 2 ; 5-15 mol % Al 2 O 3 ; 6.2-20 mol % B 2 O 3 ; 2-15 mol % Li 2 O; 0-20 mol % Na 2 O; and 0-10 mol % K 2 O, wherein the glass has a surface having a compressive layer extending from the surface to a depth of layer and is enriched in potassium cations to a second depth that is less than the depth of layer, and wherein the surface of the glass has a crack initiation layer threshold of at least 6000 gf upon indentation with a Vickers indenter, and wherein the surface has compressive stress of at least 711 MPa, wherein the glass is a glass sheet having a thickness of up to 2 mm.
9. The glass of claim 8 , further comprising lithium cations, and sodium cations.
10. The glass of claim 8 , wherein the surface has a compressive stress depth of layer is at least about 50 μm.
11. The glass of claim 8 , wherein the depth of layer is in a range from about 70 μm up to about 290 μm.
12. The glass of claim 8 , wherein the second depth is in a range from about 5 μm up to about 20 μm.
13. The glass of claim 8 , wherein the alkali aluminoborosilicate glass further comprises at least one of: 0-10 mol % P 2 O 5 ; 0-5 mol % MgO; 0-1 mol % CeO 2 ; and 0-1 mol % SnO 2 .
14. The glass of claim 8 , glass has a crack initiation layer threshold of at least 8000 gf upon indentation with a Vickers indenter.
15. An alkali aluminoborosilicate glass comprising 6.2-20 mol % B 2 O 3 , 2-8.3 mol % Li 2 O, a surface having a compressive layer extending from the surface to a depth of layer and is enriched in potassium cations to a second depth that is less than the depth of layer, wherein the surface has a compressive stress of at least 791 MPa and the depth of layer is at least about 50 μm, and wherein the surface of the glass has a crack initiation layer threshold of at least 6000 gf upon indentation with a Vickers indenter, wherein the glass is a glass sheet having a thickness of up to 2 mm.
16. The glass of claim 15 , further comprising 50-70 mol % SiO 2 ; 5-15 mol % Al 2 O 3 ; 0-20 mol % Na 2 O; and 0-10 mol % K 2 O.
17. The glass of claim 15 , wherein the depth of layer is in a range from about 70 μm up to about 290 μm, and wherein the second depth is in a range from about 5 μm up to about 20 μm.