Transparent conductive film and touch panel
A transparent conductive film having a transparent resin film containing a cyclic olefin resin and a conductive layer and having a thermal dimensional change rate in hot water at 100° C. for 60 seconds of from 0.01 to 0.2%, shows excellent adhesion between the transparent resin film and the conductive layer.
1. A transparent conductive film containing a transparent resin film and a conductive layer formed on the transparent resin film, wherein:
the transparent resin film contains a cyclic olefin resin,
the transparent conductive film has a thermal dimensional change rate in hot water at 100° C. for 60 seconds of from 0.01 to 0.2%, and
the transparent conductive film has an in-plane variation in the thermal dimensional change rate in hot water at 100° C. for 60 seconds of from 1 to 10%.
2. The transparent conductive film according to claim 1 wherein the conductive layer has an intermittent portion.
3. The transparent conductive film according to claim 1 , wherein the conductive layer contains a water soluble resin and silver.
4. The transparent conductive film according to claim 1 , wherein the transparent conductive film has a dielectric constant change rate in a temperature range of from −20 to 30° C. of from 0.1 to 10%.
5. The transparent conductive film according to claim 1 , wherein the transparent conductive film has an in-plane birefringence, Re of from 1 to 20 nm and a birefringence in the thickness direction, Rth of from 1 to 20 nm.
6. The transparent conductive film according to claim 1 , wherein the transparent conductive film has an in-plane variation in the dielectric constant change rate in a temperature range of from −20 to 30° C. of from 1 to 10%.
7. The transparent conductive film according to claim 1 , wherein the transparent conductive film has an in-plane variation in the in-plane birefringence, Re of from 1 to 10% and an in-plane variation in the birefringence in the thickness direction, Rth of from 1 to 10%.
8. The transparent conductive film according to claim 1 , wherein the transparent resin film has a thickness of from 20 to 60 μm.
9. The transparent conductive film according to claim 1 , wherein the transparent conductive film has a thickness unevenness of from 2 to 15%.
10. A touch panel containing a transparent conductive film containing a transparent resin film and a conductive layer formed on the transparent resin film, wherein the transparent resin film contains a cyclic olefin resin, and the transparent conductive film has a thermal dimensional change rate in hot water at 100° C. for 60 seconds of from 0.01 to 0.2%, and the transparent conductive film has an in-plane variation in the thermal dimensional change rate in hot water at 100° C. for 60 seconds of from 1 to 10%.