Composite casing for axial turbomachine low-pressure compressor
The invention relates to a method for manufacturing a composite casing for an axial turbomachine low-pressure compressor. The casing comprises a circular wall and a fixing flange which with the wall forms a sharp-edged corner. The method comprises the steps of: supplying a mold with a corner configured to form the edge corner of the casing; placing a filled thermoplastic resin profile section along the corner; placing a fibrous reinforcement in the mold to hug the profile section; closing the injection mold; polymerizing a resin injected into the mold and demolding the casing. The invention also relates to a composite casing with an annular wall and a flange at one end of the wall forming a sharp-edged corner on the inside of the casing. The casing is reinforced by a fibrous perform and the edge corner is reinforced with short fibers with a mean length of less than 5.00 mm.
1. A method for manufacturing a composite casing of a turbomachine, the casing comprising an arcuate wall, a fixing flange extending radially from one edge of the wall and forming with the wall a sharp-edged corner, said method comprising:
supplying a mould with a corner configured to form an edge corner of the casing;
supplying a filled thermoplastic resin profile section and placing the filled thermoplastic resin profile section along the corner of the mould, the profile section being of triangular shape;
placing a fibrous reinforcement in the mould hugging the profile section;
closing the mould;
injecting a resin into the mould such that the resin comes into contact with the profile section and polymerizing said resin in the mould, wherein during the polymerization, the resin adheres to the profile section; and
demoulding the casing.
2. The method in accordance with claim 1 , wherein during the closing of the mould, the fibrous reinforcement is pressed against the profile section.
3. The method in accordance with claim 1 , wherein the resin of the profile section comprises an epoxy-type resin.
4. The method in accordance with claim 1 , wherein the profile section comprises between 0.5 wt % and 5 wt % of carbon fibers, the carbon fibers being in contact with the resin and with the fibrous reinforcement.
5. The method in accordance with claim 1 , wherein the resin of the profile section comprises between 40 wt % and 90 wt % of N,N,N′,N′-tetraglycidyl-4,4′-diaminodiphenylmethane.
6. The method in accordance with claim 1 , wherein the resin of the profile section comprises between 10 wt % and 30 wt % of polyether sulfone.
7. The method in accordance with claim 1 , wherein the resin of the profile section comprises between 1 wt % and 10 wt % of 1,5-Naphthalenediol.
8. The method in accordance with claim 1 , wherein the resin of the profile section is a thixotropic resin.
9. The method in accordance with claim 1 , wherein the profile section has a linear mass of between 5 and 20 kg/m.