Filtering medium for air filter, filter pack, air filter unit, and method for producing filtering medium for air filter
A filtering medium includes first and second porous membranes mainly composed of fluororesin, and a plurality of air permeable supports to support the first and second membranes. The second membrane is disposed downstream of the first membrane. When air containing polyalphaolefin particles with a count median diameter of 0.25 μm is continuously passed through at a flow rate of 5.3 cm/sec and pressure loss is increased by 250 Pa, the first membrane has a dust retention amount larger than the second membrane. The filtering medium has a pressure loss of less than 200 Pa when air is passed through at a flow rate of 5.3 cm/sec. A collecting efficiency of NaCl particles with a particle diameter of 0.3 μm is 99.97% or more when air containing the NaCl particles is passed through at a flow rate of 5.3 cm/sec. The dust retention amount is 25 g/m 2 or more.
1. A filtering medium for an air filter for collecting fine particles in air, the filter medium comprising:
a first porous membrane mainly composed of a fluororesin;
a second porous membrane mainly composed of a fluororesin that is disposed on a downstream side of airflow compared to the first porous membrane; and
a plurality of air permeable supports disposed to form at least an outermost layer of the filtering medium to support the first porous membrane and the second membrane,
when air containing polyalphaolefin particles with a count median diameter of 0.25 μm is continuously passed through at a flow rate of 5.3 cm/sec and the pressure loss is increased by 250 Pa, the first porous membrane having a dust retention amount of the polyalphaolefin particles larger than the second porous membrane,
the filtering medium having a pressure loss of less than 200 Pa when the air is passed through at a flow rate of 5.3 cm/sec,
a collecting efficiency of NaCl particles with a particle diameter of 0.3 μm being 99.97% or more when the air containing the NaCl particles is passed through at a flow rate of 5.3 cm/sec, and
the dust retention amount being 25 g/m 2 or more.
2. The filtering medium for an air filter according to claim 1 , wherein
the first porous membrane has lower pressure loss than the second porous membrane and the second porous membrane has higher collecting efficiency than the first porous membrane.
3. The filtering medium for an air filter according to claim 1 , wherein
the dust retention amount of the first porous membrane is 25 to 35 g/m 2 , the pressure loss of the first porous membrane is 30 to 90 Pa, and the collecting efficiency of the first porous membrane is 95 to 99%.
4. The filtering medium for an air filter according to claim 1 , wherein
the filtering medium has a four layer structure including the first porous membrane, the second porous membrane, and two pieces of the air permeable support.
5. The filtering medium for an air filter according to claim 1 , wherein
the filtering medium has a five layer structure including the first porous membrane, the second porous membrane, and three pieces of the air permeable support, and
one piece of the air permeable support is disposed between the first porous membrane and the second porous membrane.
6. The filtering medium for an air filter according to claim 1 , wherein
the first porous membrane includes polytetrafluoroethylene which can be fibrillated, a non hot-melt processable component which cannot be fibrillated, and a hot-melt processable component having a melting point of lower than 320° C. which cannot be fibrillated.
7. A filter pack including the filtering medium for an air filter according to claim 1 , wherein
the filtering medium is processed to have a zigzag shape according to alternatively repeated outside folding and inside folding.
8. An air filter unit including the filtering medium for an air filter according to claim 1 , the air filter unit further comprising
a frame body supporting the filtering medium.
9. A method of producing a filtering medium for an air filter for collecting fine particles in air, the method comprising:
preparing a first porous membrane by using a fluororesin and a liquid lubricant;
preparing a second porous membrane to have a smaller average pore diameter than the first porous membrane by using a fluororesin and a liquid lubricant; and
producing the filtering medium by laminating the first porous membrane, the second porous membrane, and a plurality of air permeable supports which support the first porous membrane and the second porous membrane,
the producing is carried out such that the plurality of air permeable supports are disposed to form at least an outermost layer of the filtering medium,
the filtering medium having the pressure loss of less than 200 Pa,
a collecting efficiency of NaCl particles with a particle diameter of 0.3 μm being 99.97% or more when the air containing the NaCl particles is passed through at a flow rate of 5.3 cm/sec, and
the dust retention amount of polyalphaolefin being 25 g/m 2 or more when the air containing the polyalphaolefin particles with a count median diameter of 0.25 μm is continuously passed through at a flow rate of 5.3 cm/sec and the pressure loss is increased by 250 Pa.
10. The method for producing a filtering medium for an air filter according to claim 9 , wherein
the second porous membrane is prepared by using the liquid lubricant, in an amount per unit weight of the fluororesin smaller than an amount of the liquid lubricant used in preparing the first porous membrane.
11. The method for producing a filtering medium for an air filter according to claim 9 , wherein
a difference between
an amount of liquid lubricant used in preparing the first porous membrane relative to 100 parts by weight of fluororesin and
an amount of liquid lubricant which is used in preparing the first porous membrane relative to 100 parts by weight of fluororesin
is 1 to 4 parts by weight.
12. The method for producing a filtering medium for an air filter according to claim 9 , wherein
the first porous membrane is prepared by using, as the fluororesin, polytetrafluoroethylene which can be fibrillated, a non hot-melt processable component which cannot be fibrillated, and a hot-melt processable component having a melting point of lower than 320 20 C. which cannot be fibrillated.
13. The filtering medium for an air filter according to claim 2 , wherein
the dust retention amount of the first porous membrane is 25 to 35 g/m 2 , the pressure loss of the first porous membrane is 30 to 90 Pa, and the collecting efficiency of the first porous membrane is 95 to 99%.
14. The filtering medium for an air filter according to claim 2 , wherein
the filtering medium has a four layer structure including the first porous membrane, the second porous membrane, and two pieces of the air permeable support.
15. The filtering medium for an air filter according to claim 2 , wherein
the filtering medium has a five layer structure including the first porous membrane, the second porous membrane, and three pieces of the air permeable support, and
one piece of the air permeable support is disposed between the first porous membrane and the second porous membrane.
16. The filtering medium for an air filter according to claim 2 , wherein
the first porous membrane includes polytetrafluoroethylene which can be fibrillated, a non hot-melt processable component which cannot be fibrillated, and a hot-melt processable component having a melting point of lower than 320° C. which cannot be fibrillated.
17. The filtering medium for an air filter according to claim 3 , wherein
the filtering medium has a four layer structure including the first porous membrane, the second porous membrane, and two pieces of the air permeable support.
18. The filtering medium for an air filter according to claim 3 , wherein
the filtering medium has a five layer structure including the first porous membrane, the second porous membrane, and three pieces of the air permeable support, and
one piece of the air permeable support is disposed between the first porous membrane and the second porous membrane.
19. The filtering medium for an air filter according to claim 3 , wherein
the first porous membrane includes polytetrafluoroethylene which can be fibrillated, a non hot-melt processable component which cannot be fibrillated, and a hot-melt processable component having a melting point of lower than 320° C. which cannot be fibrillated.
20. An air filter unit including the filter pack according to claim 7 , the air filter unit further comprising
a frame body supporting the filter pack.