Method for producing a masterbatch of synthetic diene elastomer and carbon-based filler
View Patent ↗A method for preparing a masterbatch of synthetic elastomer and of carbon-based filler, which comprises the following steps: preparing an aqueous dispersion of carbon-based filler having a zeta potential with the opposite sign to that of an anionic or cationic synthetic elastomer latex, the difference between the potentials of the anionic or cationic elastomer latex and the aqueous dispersion of carbon-based filler being such that the absolute value thereof is greater than or equal to 20 mV, bringing together, and mixing, the anionic or cationic synthetic elastomer latex and the aqueous dispersion of carbon-based filler to obtain a coagulum, recovering the coagulum, and drying the recovered coagulum in order to obtain the masterbatch.
1. A method for preparing a masterbatch of synthetic elastomer and of carbon-based filler, which comprises the following steps:
preparing an aqueous dispersion of carbon-based filler having a zeta potential with the opposite sign to that of an anionic or cationic synthetic elastomer latex, the difference between the potentials of the anionic or cationic elastomer latex and the aqueous dispersion of carbon-based filler being such that the absolute value thereof is greater than or equal to 20 mV;
bringing together, and mixing, the anionic or cationic synthetic elastomer latex and the aqueous dispersion of carbon-based filler to obtain a coagulum;
recovering the coagulum; and
drying the recovered coagulum in order to obtain the masterbatch.
2. The method according to claim 1 , wherein the synthetic elastomer is a synthetic diene elastomer.
3. The method according to claim 1 , wherein the difference between the zeta potentials of the anionic or cationic elastomer latex and of the aqueous dispersion of carbon-based filler has an absolute value which is greater than or equal to 30 mV.
4. The method according to claim 1 , wherein the aqueous dispersion of carbon-based filler contains a surfactant with the opposite sign to that of the synthetic elastomer latex.
5. The method according to claim 1 , wherein the anionic or cationic synthetic elastomer latex contains at least one surfactant, respectively anionic or cationic.
6. The method according to claim 1 , wherein the synthetic elastomer latex is obtained by aqueous phase polymerization.
7. The method according to claim 6 , wherein the synthetic elastomer latex is obtained by aqueous phase emulsification of a diene elastomer.
8. The method according to claim 1 , wherein the synthetic elastomer latex is a latex of butadiene and stirene copolymer, SBR.
9. The method according to claim 8 , wherein the synthetic elastomer latex is an SBR prepared in emulsion.
10. The method according to claim 1 , wherein the amount of carbon-based filler during the bringing together of the two aqueous dispersions ranges from 2 phom to 150 phom, parts by weight per hundred parts of organic matter.
11. The method according to claim 10 , wherein the carbon-based filler comprises carbon black.
12. The method according to claim 11 , wherein the carbon-based filler consists of carbon black.
13. The method according to claim 11 , wherein the amount of carbon-based filler during the bringing together of the two aqueous dispersions ranges from 30 phom to 110 phom.
14. The method according to claim 13 , wherein the amount of carbon-based filler during the bringing together of the two aqueous dispersions ranges from 40 phom to 100 phom.
15. A masterbatch of synthetic diene elastomer and of carbon-based filler, obtained according to claim 1 .
16. An elastomer composition based on at least one masterbatch according to claim 15 .
17. A finished or semi-finished article comprising a composition according to claim 16 .
18. A tire tread comprising a composition according to claim 16 .
19. A tire or semi-finished product comprising at least one rubber composition according to claim 16 .