Electrode material and secondary cell
An electrode material for a secondary cell includes a porous carbon material having an absolute value of a differential value of a mass using a temperature as a parameter exceeding 0 at 360° C. and being 0.016 or more at 290° C. provided by thermally analyzing a mixture of the porous carbon material and S 8 sulfur at a mass ratio of 1:2.
1. A secondary cell, comprising:
an electrode material, comprising a porous carbon material having an absolute value of a differential value of a mass with respect to a differential value of a temperature exceeding 0 at 360° C. and being 0.016 or more at 290° C. provided by thermogravimetrically analyzing a mixture of the porous carbon material and S 8 sulfur at a mass ratio of 1:2,
wherein the secondary cell is a lithium-sulfur secondary cell, and
wherein the electrode material supports sulfur or a sulfur compound.
2. The secondary cell according to claim 1 , wherein
the porous carbon material includes a plant-derived material containing 5% by mass or more of silicon as a raw material.
3. The secondary cell according to claim 1 , wherein
the porous carbon material includes a peat or a wood-based material as a raw material.
4. The secondary cell according to claim 1 , wherein
the porous carbon material has a surface area of 10 m2/g or more by a nitrogen BET method, and has a pore volume of 0.1 cm3/g or more by a BJH method and an MP method.
5. The secondary cell according to claim 1 , wherein
the porous carbon material has a half-value width of 5 degrees or less based on a diffraction angle of 2θ in a diffraction intensity peak of a (100) face or a (101) face by an X ray diffractometry.
6. The secondary cell according to claim 1 , wherein
the electrode material is configured as a cathode.