Film and method for packaging a compressible product in a compressed state and packaged compressible product
The present invention relates to a method for packaging a compressible product in a compressed state, comprising the step of sealing at least two parts of a polymeric machine direction oriented (MDO) film which encloses at least part of the compressible product in the compressed state, characterized in that the seal has a seal elongation at failure of about 20% to about 100%, as measured in accordance with ASTM F88/F88M-09. The present invention also relates to a compressible product in a compressed state packaged in a polymeric MDO film which encloses at least part of the compressible product, wherein at least two parts of the MDO film are sealed and characterized in that the seal has a seal elongation at failure of about 20% to about 100%, as measured in accordance with ASTM F88/F88M-09.
1. A polymeric machine direction oriented (MDO) film for packaging a compressible product in a compressed state, characterised in that the MDO film, when at least two parts of the MDO film are sealed, provides a seal with a seal elongation at failure of about 20% to about 100%, as measured in accordance with ASTM F88/F88M-09, wherein the MDO film has an elongation at break in the machine direction of about 100% to about 300%, as measured in accordance with ASTM D882, and the MDO film comprises from about 1% to about 90% by weight of one or more polymers selected from the group consisting of high density polyethylene (HDPE), medium density polyethylene (MDPE), cyclic olefin copolymer (COC), and styrene butadiene copolymer (SBC), with % by weight relative to the total weight of the MDO film.
2. The MDO film according to claim 1 , wherein the seal has a seal elongation at failure of about 25% to about 100%, as measured in accordance with ASTM F88/F88M-09.
3. The MDO film according to claim 1 , wherein the sealing comprises heat sealing.
4. The MDO film according to claim 1 , wherein the MDO film has a tensile creep in the machine direction of about 0.10% to about 0.50% per μm thickness of the film, as measured in accordance with ISO 899-1-2003 with following conditions: sample width of 15 mm, grip distance of 100 mm, a load of 2300 g, 24 hours, and at 23° C.
5. The MDO film according to claim 1 , wherein the MDO film has a thickness of about 15 μm to about 100 μm.
6. The MDO film according to claim 1 , wherein the MDO film has an elongation at break in the machine direction of about 150% to about 250%, as measured in accordance with ASTM D882.
7. The MDO film according to claim 1 , wherein the seal has a seal elongation at failure of about 30% to about 90%, as measured in accordance with ASTM F88/F88M-09.
8. The MDO film according to claim 1 , wherein the seal has a seal elongation at failure of about 35% to about 80%, as measured in accordance with ASTM F88/F88M-09.
9. The MDO film according to claim 1 , wherein the MDO film comprises from about 5% to about 85% by weight of the one or more polymers selected from the group consisting of HDPE, MDPE, COC, and SBC.
10. The MDO film according to claim 1 , wherein the MDO film comprises from about 10% to about 80% by weight of the one or more polymers selected from the group consisting of HDPE, MDPE, COC, and SBC.
11. A method for packaging a compressible product in a compressed state, comprising the step of sealing at least two parts of the polymeric machine direction oriented (MDO) film as defined in claim 1 which encloses at least part of the compressible product in the compressed state, characterised in that the seal has a seal elongation at failure of about 20% to about 100%, as measured in accordance with ASTM F88/F88M-09.
12. The method according to claim 11 , wherein the seal has a seal elongation at failure of about 25% to about 100%, as measured in accordance with ASTM F88/F88M-09.
13. The method according to claim 11 , wherein the sealing comprises heat sealing.
14. The method according to claim 11 , wherein the compressible product is an insulation product.
15. The method according to claim 11 , wherein the compressible product is a mineral wool product.
16. The method according to of claim 11 , wherein the MDO film has a tensile creep in the machine direction of about 0.10% to about 0.50% per μm thickness of the film, as measured in accordance with ISO 899-1-2003 with following conditions: sample width of 15 mm, grip distance of 100 mm, a load of 2300 g, 24 hours, and at 23° C.
17. The method according to claim 11 , wherein the MDO film has a thickness of about 15 μm to about 100 μm.
18. The method according to claim 11 , wherein the MDO film has an elongation at break in the machine direction of about 150% to about 250%, as measured in accordance with ASTM D882.
19. A compressible product in a compressed state packaged in the polymeric machine direction oriented (MDO) film as defined in claim 1 which encloses at least part of the compressible product, wherein at least two parts of the MDO film are sealed and characterised in that the seal has a seal elongation at failure of about 20% to about 100%, as measured in accordance with ASTM F88/F88M-09.
20. The packaged product according to claim 19 , wherein the seal has a seal elongation at failure of about 25% to about 100%, as measured in accordance with ASTM F88/F88M-09.
21. The packaged product according to claim 19 , wherein the sealing comprises heat sealing.
22. The packaged product according to claim 19 , wherein the compressible product is an insulation product.
23. The packaged product according to claim 19 , wherein the compressible product is a mineral wool product.
24. The packaged product according to claim 19 , wherein the MDO film has a tensile creep in the machine direction of about 0.10% to about 0.50% per μm thickness of the film, as measured in accordance with ISO 899-1-2003 with following conditions: sample width of 15 mm, grip distance of 100 mm, a load of 2300 g, 24 hours, and at 23° C.
25. The packaged product according to claim 19 , wherein the MDO film has a thickness of about 15 μm to about 100 μm.
26. The packaged product according to claim 19 , wherein the MDO film has an elongation at break in the machine direction of about 150% to about 250%, as measured in accordance with ASTM D882.