High modulus glass fibre composition, and glass fibre and composite material thereof
A high-modulus glass fiber composition, and a glass fiber and a composite material therefrom. The glass fiber composition comprises the following components in weight percentage: SiO 2 55.7 to 58.9%, Al 2 O 3 15 to 19.9%, Y 2 O 3 0.1 to 4.3%, La 2 O 3 less than or equal to 1.5%, CeO 2 less than or equal to 1.2%, CaO 6 to 10%, MgO 9.05 to 9.95%, SrO less than or equal to 2%, Li 2 O+Na 2 O+K 2 O less than or equal to 0.99%, Li 2 O less than or equal to 0.65%, Fe 2 O 3 less than 1%, TiO 2 0.1 to 1.5%; wherein, the range of the weight percentage ratio C1=Y 2 O 3 /(Y 2 O 3 +La 2 O 3 +CeO 2 ) is greater than 0.6. The composition can greatly improve the elastic modulus of glass, significantly reduce liquidus temperature and forming temperature of the glass, greatly reduce the crystallization rate of molten glass and bubble amount under the same conditions, and therefore is more suitable for large-scale tank furnace production of high-modulus fiberglass with low bubble amount.
1. A high-modulus glass fiber composition comprising the following components expressed as weight percentage:
SiO 2
55.7-58.9%
Al 2 O 3
15-19.9%
Y 2 O 3
0.1-4.3%
La 2 O 3
less than or equal to 1.5%
CeO 2
less than or equal to 1.2%
CaO
6-10%
MgO
9.05-9.95%
SrO
less than or equal to 2%
Li 2 O + Na 2 O + K 2 O
less than or equal to 0.99%
Li 2 O
less than or equal to 0.65%
Fe 2 O 3
less than 1%
TiO 2
0.1-1.5%
wherein, the range of the weight percentage ratio C1=Y 2 O 3 /(Y 2 O 3 +La 2 O 3 +CeO 2 ) is greater than 0.6, the range of total content of La 2 O 3 +CeO 2 expressed as weight percentage is 0.1-2%, the range of weight percentage ratio C2=SiO 2 /CaO is 5.8-9.3, and the range of weight percentage ratio C3=MgO/(CaO+SrO) is 0.9-1.6.
2. The high-modulus glass fiber composition of claim 1 , wherein the content of Li 2 O expressed as weight percentage is 0.05-0.55%.
3. The high-modulus glass fiber composition of claim 1 , wherein the content of Y 2 O 3 expressed as weight percentage is 0.5-3.9%.
4. The high-modulus glass fiber composition of claim 1 , wherein the content of Y 2 O 3 expressed as weight percentage is 1.3-3.9%.
5. The high-modulus glass fiber composition of claim 1 , wherein the content of La 2 O 3 expressed as weight percentage is 0.05-1.2%.
6. The high-modulus glass fiber composition of claim 1 , wherein the content of CeO 2 expressed as weight percentage is 0.05-1%.
7. The high-modulus glass fiber composition of claim 1 , wherein the content of CaO expressed as weight percentage is 8-9.3%.
8. The high-modulus glass fiber composition of claim 1 , wherein the total content of Li 2 O+Na 2 O+K 2 O expressed as weight percentage is 0.4-0.94%.
9. The high-modulus glass fiber composition of claim 1 , wherein the total content of Y 2 O 3 +La 2 O 3 +CeO 2 expressed as weight percentage is 1.4-4.2%.
10. The high-modulus glass fiber composition of claim 1 comprising the following components expressed as weight percentage:
SiO 2
55.7-58.9%
Al 2 O 3
15-19.9%
Y 2 O 3
0.1-4.3%
La 2 O 3
less than or equal to 1.5%
CeO 2
less than or equal to 1.2%
CaO
6-10%
MgO
9.05-9.95%
SrO
less than or equal to 2%
Li 2 O + Na 2 O + K 2 O
less than or equal to 0.99%
Li 2 O
less than or equal to 0.65%
Fe 2 O 3
less than 1%
TiO 2
0.1-1.5%
wherein, the range of the weight percentage ratio C1=Y 2 O 3 /(Y 2 O 3 +La 2 O 3 +CeO 2 ) is greater than 0.6, the range of the weight percentage ratio C2=SiO 2 /CaO is 5.8-9.3, and the range of the weight percentage ratio C3=MgO/(CaO+SrO) is 0.9-1.6.
11. The high-modulus glass fiber composition of claim 1 comprising the following components expressed as weight percentage:
SiO 2
55.7-58.9%
Al 2 O 3
15-19.9%
Y 2 O 3
0.1-4.3%
La 2 O 3
0.05-1.2%
CeO 2
0.05-1%
La 2 O 3 + CeO 2
0.1-2%
CaO
6-10%
MgO
9.05-9.95%
SrO
less than or equal to 2%
Li 2 O + Na 2 O + K 2 O
less than or equal to 0.99%
Li 2 O
less than or equal to 0.65%
Fe 2 O 3
less than 1%
TiO 2
0.1-1.5%
wherein, the range of the weight percentage ratio C1=Y 2 O 3 /(Y 2 O 3 +La 2 O 3 +CeO 2 ) is greater than 0.7, the range of the weight percentage ratio C2=SiO 2 /CaO is 6.3-8.5, and the range of the weight percentage ratio C3=MgO/(CaO+SrO) is 1-1.5.
12. The high-modulus glass fiber composition of claim 1 comprising the following components expressed as weight percentage:
SiO 2
55.7-58.9%
Al 2 O 3
15-19.9%
Y 2 O 3
0.5-3.9%
La 2 O 3
0.05-1.2%
CeO 2
0.05-1%
La 2 O 3 + CeO 2
0.1-2%
CaO
6-10%
MgO
9.05-9.95%
SrO
less than or equal to 2%
Li 2 O + Na 2 O + K 2 O
less than or equal to 0.99%
Li 2 O
less than or equal to 0.65%
Fe 2 O 3
less than 1%
TiO 2
0.1-1%
wherein, the range of the weight percentage ratio C1=Y 2 O 3 /(Y 2 O 3 +La 2 O 3 +CeO 2 ) is 0.75-0.97, the range of the weight percentage ratio C2=SiO 2 /CaO is 6.3-8.5, and the range of the weight percentage ratio C3=MgO/(CaO+SrO) is 1-1.5.
13. The high-modulus glass fiber composition of claim 1 , wherein the range of the weight percentage ratio C1=Y 2 O 3 /(Y 2 O 3 +La 2 O 3 +CeO 2 ) is 0.75-0.97.
14. The high-modulus glass fiber composition of claim 1 , wherein the range of the weight percentage ratio C4=La 2 O 3 /CeO 2 is greater than 1.
15. A glass fiber being produced from the glass fiber composition described in claim 1 .
16. A composite material incorporating the glass fiber described in claim 15 .