Silicon-silicon oxide-lithium composite material having nano silicon particles embedded in a silicon:silicon lithium silicate composite matrix, and a process for manufacture thereof
A process for producing a silicon:silicon oxide:lithium composite (SSLC) material useful as a negative electrode active material for non-aqueous battery cells includes: producing a partially lithiated SSLC material by way of mechanical mixing; subsequently producing a further prelithiated SSLC material by way of spontaneous lithiation procedure; and subsequently producing a delithiated SSLC material by way of reacting lithium silicide within the dispersed prelithiated SSLC material with organic solvent(s) to extract lithium from the prelithiated SSLC material, until reactivity of lithium silicide within the prelithiated SSLC material with the organic solvent(s) ceases. The delithiated SSLC material is a porous plastically deformable matrix having nano silicon embedded therein. The delithiated SSLC material can have a lithium silicide content of less than 0.5% by weight. A battery cell having as its negative electrode active material an SSLC material as set forth herein can exhibit an irreversible capacity loss of less than 10%.
1. A completely delithiated silicon:silicon oxide:lithium composite (SSLC) material for use as a lithium ion battery secondary cell negative electrode, the SSLC material having a silicon content of 30%-60% by weight, a lithium content of 10%-20% by weight, an oxygen content of 25%-40% by weight, and a lithium silicide content of less than 0.5% by weight uniformly distributed therein.
2. The SSLC material of claim 1 , wherein the lithium ion battery secondary cell exhibits an irreversible capacity loss of less than 15%.
3. The SSLC material of claim 2 , wherein the lithium ion secondary battery cell exhibits an irreversible capacity loss of less than 12%.
4. The lithium ion battery secondary cell of claim 2 , wherein an anode thereof exhibits a volume change of 10-35% in association with the lithium ion battery secondary cell charging and discharging.
5. The lithium ion battery secondary cell of claim 4 , wherein the anode exhibits an average volume change of 20% in association with the lithium ion battery secondary cell charging and discharging.
6. The SSLC material of claim 1 , wherein the delithiated SSLC material has a particle size of 1-10 μm.
7. The SSLC material of claim 1 , wherein the silicon content comprises nano silicon particles having a particle size of 5-150 nm.