Solid catalyst for hydride isomerization reaction in an aqueous medium
A novel catalyst capable of selectively catalyzing conversion from glucose to fructose in water or in an aqueous solution is provided. The catalyst is a solid catalyst for a hydride isomerization reaction from glucose to fructose performed in water or in an aqueous solution, comprising a group 13 element oxide whose surface has been subjected to a phosphoric acid treatment.
1. A method for selectively producing fructose as a produced product from glucose as a raw material, the method comprising:
conducting a catalytic hydride isomerization reaction from glucose to fructose in the presence of a solid catalyst in water or in an aqueous solution,
obtaining the produced product from the water or the aqueous solution,
wherein the solid catalyst consists essentially of a Group 13 element oxide whose surface is bonded with a phosphoric acid to form a structure of —O—P(O)(OH) 2 with the Group 13 element oxide.
2. The method according to claim 1 , wherein the produced product comprises fructose and mannose, and wherein the production of fructose from glucose has a selectivity ratio of at least 42.1%.
3. The method according to claim 1 , wherein the Group 13 element oxide is at least one selected from the group consisting of aluminum oxide, gallium oxide, indium oxide and thallium oxide.
4. The method according to claim 1 , wherein the Group 13 element oxide is obtained by treating an untreated Group 13 element oxide in a phosphoric acid aqueous solution at 50° C. or lower.
5. The method according to claim 1 , wherein a Lewis acid is contained in the Group 13 element oxide whose surface is bonded with a phosphoric acid to form the structure of —O—P(O)(OH) 2 with the Group 13 element oxide, and wherein an amount of the Lewis acid in the Group 13 element oxide whose surface is bonded with a phosphoric acid to form the structure of —O—P(O)(OH) 2 with the Group 13 element oxide and which has been subjected to a phosphoric acid treatment is kept, in a state where the surface of the Group 13 element oxide is hydrated, at 80% or more of an amount of a Lewis acid in a Group 13 element oxide whose surface has not been subjected to a phosphoric acid treatment and has been dehydrated.
6. The method according to claim 1 , wherein the surface of the Group 13 element oxide is bounded with the phosphoric acid in a phosphoric acid aqueous solution at 50° C. or lower to form the structure of —O—P(O)(OH) 2 with the Group 13 element oxide.
7. The method according to claim 1 , wherein the Group 13 element oxide has a surface on which from 0.0001 to 0.003 mol % of the phosphoric acid is immobilized.
8. The method according to claim 1 , wherein the surface of the Group 13 element oxide is bounded with the phosphoric acid in a phosphoric acid aqueous solution at 50° C. or lower to form the structure of —O—P(O)(OH) 2 with the Group 13 element oxide, and wherein the Group 13 element oxide has a surface on which from 0.0001 to 0.003 mol % of the phosphoric acid is immobilized.