Biodegradable polymer recycling
A biodegradable material is capable of recovery and recycling by dissolution in water at a temperature 40° C. or higher. The material is insoluble in water at 25° C. The material includes one or both of virgin or scrap polyvinyl alcohol material resultant from manufacture of an article composed of polyvinyl alcohol, or a waste stream containing polyvinyl alcohol material.
1. A process for recovery of a waste polymer comprising the steps of:
collecting waste polymer material including unmodified polyvinyl alcohol having a degree of hydrolysis of at least 98 mol %;
dissolving the unmodified polyvinyl alcohol in water at a temperature in the range of 60° C. or greater to give a solution of the polyvinyl alcohol;
separating any residual solid phase to form a filtered solution;
either reformulating the unmodified polyvinyl alcohol solution for a secondary use or mixing the filtered solution with a precipitant to recover the unmodified polyvinyl alcohol as a precipitate; and separating the precipitated unmodified polyvinyl alcohol for re-formulating and recycling, wherein the precipitant is selected from the group consisting of alcohols, ketones and mixtures thereof.
2. The process as claimed in claim 1 , wherein the precipitant is ethanol or acetone.
3. A process for recovery of a waste polymer comprising the steps of:
collecting waste polymer material including unmodified polyvinyl alcohol having a degree of hydrolysis of at least 98 mol %;
dissolving the unmodified polyvinyl alcohol in water at a temperature in the range of 60° C. or greater to give a solution of the polyvinyl alcohol;
separating any residual solid phase to form a filtered solution;
either reformulating the unmodified polyvinyl alcohol solution for a secondary use or mixing the filtered solution with a precipitant to recover the unmodified polyvinyl alcohol as a precipitate; and separating the precipitated unmodified polyvinyl alcohol for re-formulating and recycling, wherein the amount of the precipitant is in the range of 50% to 100% by weight of the aqueous solution.
4. The process as claimed in claim 3 , wherein the amount of the precipitant is in the range of 50% to 70% by weight of the aqueous solution.
5. A process for recovery of a waste polymer comprising the steps of:
collecting waste polymer material including unmodified polyvinyl alcohol having a degree of hydrolysis of at least 98 mol %;
dissolving the unmodified polyvinyl alcohol in water at a temperature in the range of 60° C. or greater to give a solution of the polyvinyl alcohol;
separating any residual solid phase to form a filtered solution;
either reformulating the unmodified polyvinyl alcohol solution for a secondary use or mixing the filtered solution with a precipitant to recover the unmodified polyvinyl alcohol as a precipitate; and separating the precipitated unmodified polyvinyl alcohol for re-formulating and recycling, wherein the unmodified polyvinyl alcohol has substantially no functionality besides hydroxyl and acetate groups.