Separator for battery
A separator for batteries that achieves both adhesiveness to electrodes and low thermal shrinkage, which have been conventionally difficult to be compatible with each other, and has excellent ion permeability in order to further improve the safety of the separator, on the assumption that lithium ion secondary batteries are widely used for electric automobiles and the like, which require the batteries to withstand severe operating conditions. The separator for batteries is configured such that a modified porous layer containing a fluororesin and inorganic particles is laminated on at least one side of a porous membrane formed of a polyolefin resin. The content of the particles is equal to or more than 40% by volume and less than 70% volume with respect to the total of the fluororesin and the particles. The fluororesin has a crystallinity of equal to or more than 36% and less than 70%.
1. A separator for batteries comprising:
a porous membrane formed of a polyolefin resin; and
a modified porous layer including a fluororesin and inorganic particles laminated on at least one side of the porous membrane,
wherein the fluororesin is consisting of a polyvinylidene fluoride-hexafluoro propylene copolymer,
a content of the particles is equal to or more than 40% by volume and less than 70% volume with respect to a total of the fluororesin and the particles,
the fluororesin has a crystallinity of equal to or more than 36% and less than 70%, and
a weight-average molecular weight (Mw) of the fluororesin is equal to or more than 0.9×10 6 and less than 1.5×10 6 .
2. The separator for batteries of claim 1 , the separator satisfying Formula (1):
20≤Y−X≤100 Formula (1)
where X is an air permeation resistance (sec/100 cc Air) of the porous membrane, and
Y is an air permeation resistance (sec/100 cc Air) of whole of the separator for batteries (sec/100 cc Air).
3. The separator for batteries of claim 1 , wherein the polyolefin porous membrane has a thickness of not more than 25 μm.
4. The separator for batteries of claim 1 , wherein the inorganic particles include at least one selected from the group consisting of alumina, titania, boehmite, and barium sulfate.
5. The separator for batteries of claim 1 , the separator being used as a separator for lithium ion secondary batteries.
6. The separator for batteries of claim 1 , wherein the content of the particles is equal to or more than 45% by volume and less than 65% volume with respect to a total of the fluororesin and the particles.