Use of olivine catalysts for carbon dioxide reforming of methane
Disclosed are metal oxide catalysts, and methods for their use, that includes a bulk metal oxide catalyst composed of at least two metals and nesosilicate. The catalyst is capable of catalyzing the carbon dioxide reforming of methane to produce hydrogen and carbon monoxide.
1. A bulk metal oxide catalyst capable of producing hydrogen (H 2 ) and carbon monoxide (CO) from methane (CH 4 ) and carbon dioxide (CO 2 ), wherein the bulk metal oxide catalyst consists of an olivine structure having a crystal lattice that has discrete SiO 4 anions and two metals (M 1 , M 2 ) or three metals (M 1 , M 2 , M 3 ) in the crystal lattice, where each SiO 4 4− has a Si cation and four O − anions
M 2 is a dry reforming of methane catalytic metal, and
the O − anions are coordinated with the metals in the crystal lattice, and wherein the bulk metal oxide catalyst does not include a carrier or a support.
2. The bulk metal oxide catalyst of claim 1 , wherein M 1 comprises at least one metal from Groups IIA, VIB, VIIB, VIII, and Group IB or at least one compound thereof, and M 2 comprises at least one metal from Group IIIB, IVB, VIB, VIII or at least one compound thereof, or at least one lanthanide or at least one compound thereof, wherein M 1 and M 2 are different.
3. The bulk metal oxide catalyst of claim 1 , wherein M 2 comprises nickel (Ni), scandium (Sc), zirconium (Zr), molybdenum (Mo), chromium (Cr), ruthenium (Ru), osmium (Os), rhodium (Rh), iridium (Ir), platinum (Pt), copper (Cu), palladium (Pd), dysprosium (Dy), thulium (Tm), ytterbium (Yb), lutetium (Lu), cerium (Ce), or any compound thereof.
4. The bulk metal oxide catalyst of claim 1 , wherein M 1 comprises manganese (Mn), magnesium (Mg), calcium (Ca) or any compound thereof.
5. The bulk metal oxide catalyst of claim 1 , wherein M 1 comprises Mg or a compound thereof, or Ca or a compound thereof, and M 2 comprises Ni or a compound thereof.
6. The bulk metal oxide catalyst of claim 1 , wherein M 3 comprises a metal from Group VIII or a compound thereof, Group IB or a compound thereof, or both, and wherein M 1 , M 2 and M 3 are different.
7. The bulk metal oxide catalyst of claim 6 , wherein M 3 comprises Pt, Ru, Rh, Ir, Au, Ag, Pd or any compounds thereof.
8. The bulk metal oxide catalyst of claim 1 , wherein the bulk metal oxide catalyst is represented by the formula of (M 1 (1-x) M 2 x ) 2 SiO 4 , where 0<x≤0.5, and M 1 and M 2 are different.
9. The bulk metal oxide catalyst of claim 8 , wherein M 1 is Mg or Ca, and M 2 is Ni.
10. The bulk metal oxide catalyst of claim 9 , wherein the bulk metal oxide catalyst is (Mg 0.5 Ni 0.5 ) 2 SiO 4 , or (Ca 0.5 Ni 0.5 ) 2 SiO 4 .
11. The bulk metal oxide catalyst of claim 1 , wherein the bulk metal oxide catalyst is represented by the formula of (M 1 (1-x) M 2 x M 3 y ) 2 SiO 4 , where 0<x≤0.5, 0<y≤0.05 and (x+y)≤0.5, and M 1 , M 2 , and M 3 are different.
12. The bulk metal oxide catalyst of claim 11 , wherein M 1 is Mg or Ca, M 2 is Ni, and M 3 is Pt, Ru, Rh, or Ir.
13. The bulk metal oxide catalyst of claim 12 , wherein the bulk metal oxide catalyst has the formula of (Ni 0.5 Mg 0.5 M 3 0.01 ) 2 SiO 4 , where M 3 is Pt, Ru, Rh, or Ir.
14. The bulk metal oxide catalyst of claim 11 , wherein the bulk metal oxide catalyst crystal structure comprises a hexagonal closest packed arrays of the O − , a octahedral interstices, and a tetrahedral interstices, wherein one-half of the octahedral interstices are occupied by M 1 cations, M 2 cations, and/or M 3 cations, and one-eighth of the tetrahedral interstices are occupied by Si cations (Si + ).
15. The bulk metal oxide catalyst of claim 1 , wherein M 2 is Ni.
16. A method of making a bulk metal oxide catalyst of claim 1 , the method comprising:
(a) mixing M 1 , M 2 , and silicon dioxide (SiO 2 ) to form a mixture; and
(b) subjecting the mixture to conditions such that M 1 , M 2 , and SiO 2 form the bulk metal oxide catalyst.
17. The method of claim 16 , wherein the mixture is molded to form a molded mixture, and wherein conditions comprise:
(a) heating the molded mixture to a temperature of about 1300° C. at a rate of 1° C.;
(b) holding the molded mixture at temperature of about 1300° C. for about 24 hours;
(c) cooling the hot molded mixture at a rate of about 1° C. to room temperature;
(d) crushing and grinding the molded mixture from step (c); and
(e) repeating steps (a) to (d).
18. A method of producing a gaseous mixture comprising contacting a reactant gas mixture comprising methane and an oxidant with the bulk metal oxide catalyst of claim 1 at a temperature of at least 800° C. to produce a gaseous mixture comprising hydrogen and carbon monoxide, wherein the catalyst is resistant to coke formation.
19. The method of claim 18 , wherein the oxidant is carbon dioxide.