Modified polyvinyl alhohol, resin composition, and film
A modified PVA that enables formation of a film superior in cold water solubility, mechanical strength, and chemical resistance is provided. The modified PVA comprises a monomer unit represented by formula (I), and a structural unit represented by formula (II): wherein: a content of the monomer unit (I) is from 0.05 mol % to 10 mol %, and a content of the structural unit (II) is from 0.001 mol % to 0.5 mol % with respect to the total monomer units in the modified PVA; a viscosity average degree of polymerization is from 300 to 3,000; and a degree of saponification is from 82 mol % to 99.5 mol %. In the formula (I): R 1 represents a hydrogen atom, or a methyl group; and R 2 represents —R 3 —SO 3 − X + , —R 3 —N + (R 4 ) 3 Cl − , or a hydrogen atom, R 3 representing an alkanediyl group, X + representing a hydrogen atom, a metal atom, or an ammonium group, and R 4 representing an alkyl group.
1. A film comprising a resin composition, said resin composition comprising a modified polyvinyl alcohol and a plasticizer,
wherein the modified polyvinyl alcohol comprises a monomer unit represented by formula (I), and a structural unit represented by formula (II):
wherein in the formula (I),
R 1 represents a hydrogen atom, or a linear or branched alkyl group having 1 to 8 carbon atoms, and
R 2 represents —R 3 —SO 3 − X + , —R 3 —N + (R 4 ) 3 Cl − , or a hydrogen atom,
R 3 representing a linear or branched alkanediyl group having 1 to 10 carbon atoms,
X + representing a hydrogen atom, a metal atom, or an ammonium group, and
R 4 representing a linear or branched alkyl group having 1 to 5 carbon atoms, wherein a plurality of R 4 s are identical or different; and
wherein in the formula (II),
R 5 represents a hydrogen atom, or a linear or branched alkyl group having 1 to 8 carbon atoms,
wherein:
a percentage content of the monomer unit represented by the formula (I) with respect to total monomer units in the modified polyvinyl alcohol is 0.05 mol % or greater and 10 mol % or less;
a percentage content of the structural unit represented by the formula (II) with respect to the total monomer units in the modified polyvinyl alcohol is 0.001 mol % or greater and 0.5 mol % or less;
a viscosity average degree of polymerization is 300 or greater and 3,000 or less;
a degree of saponification is 82 mol % or greater and 99.5 mol % or less;
a content of the plasticizer with respect to 100 parts by mass of the modified polyvinyl alcohol is 15 parts by mass or greater and 50 parts by mass or less; and
a time period required for a 40 mm×40 mm square of said film having an average thickness of 50 μm to be completely dissolved in 10° C. water is less than 45 sec, converted where the average thickness of the film is not 50 μm according to the following equation:
converted time period (sec)=(50/Average thickness of film (μm)) 2 ×Measured time period (sec).
2. The film according to claim 1 , wherein R 2 represents —R 3 —N + (R 4 ) 3 Cl − .
3. The film according to claim 1 , wherein R 2 represents a hydrogen atom.
4. The film according to claim 1 , wherein said film consists of said resin composition.
5. The film according to claim 4 , wherein R 2 represents —R 3 —N + (R 4 ) 3 Cl − .
6. The film according to claim 4 , wherein R 2 represents a hydrogen atom.
7. The film according to claim 1 , wherein the time period required for a 40 mm×40 mm square of said film having an average thickness of 50 μm to be completely dissolved in 10° C. water is less than 30 sec.
8. The film according to claim 4 , wherein the time period required for a 40 mm×40 mm square of said film having an average thickness of 50 μm to be completely dissolved in 10° C. water is less than 30 sec.