Non-hot-melt MDI-based polyurethane composition bearing NCO end groups and having a low content of MDI monomer, comprising at least one isocyanate compound of particular molar volume
1) Polyurethane composition comprising: a) at least 98% by weight of at least one non-hot-melt polyurethane bearing NCO end groups based on diphenyl methane diisocyanates (MDI), b) a MDI monomer content of less than or equal to 1% by weight, c) at least one particular isocyanate compound with a molar volume of less than or equal to 300 milliliters per mole. 2) Process for preparing a polyurethane composition as defined previously, and an adhesive, mastic and/or surface coating composition formulated from such a polyurethane composition.
1. A process for the preparation of a composition comprising:
a) at least 98% by weight of at least one non-hot-melt polyurethane bearing NCO end groups based on diphenylmethane diisocyanate noted MDI
b) a content of MDI monomer of less than or equal to 1% by weight,
c) at least one isocyanate compound with a molar volume of less than or equal to 300 milliliters per mole noted compound A, in which the isocyanate group or groups are not linked to a carbon atom of an aromatic hydrocarbon-based ring,
the weight percentages being expressed relative to the total weight of the polyurethane composition, said process, comprising a step in which the compound or compounds A and other ingredient or ingredients optionally present in said composition, are mixed with a polyurethane composition comprising at least one polyurethane bearing NCO end groups based on MDI, which is not solid at a temperature ranging from 5 to 35° C., and a MDI content of less than or equal to 1% by weight relative to the weight of said polyurethane composition, at a temperature of less than or equal to 50° C., under anhydrous conditions in post-synthesis of said MDI-based polyurethane bearing NCO end groups.
2. The process according to claim 1 wherein the compound(s) (A) are mixed with said composition:
either directly after the end of the reaction for the synthesis of the polyurethane bearing NCO end groups based on MDI,
or after one, several or all of the other ingredients of the composition have been mixed with the polyurethane bearing NCO end groups based on MDI.
3. A process for the preparation of a composition comprising:
a) at least 98% by weight of at least one non-hot-melt polyurethane bearing NCO end groups based on diphenylmethane diisocyanate noted MDI
b) a content of MDI monomer of less than or equal to 1% by weight,
c) at least one isocyanate compound with a molar volume of less than or equal to 300 milliliters per mole noted compound A, in which the isocyanate group or groups are not linked to a carbon atom of an aromatic hydrocarbon-based ring, compound A being an aliphatic, acyclic, linear or branched monoisocyanate, benzyl monoisocyanate, cycloaliphatic monoisocyanate, benzyl diisocyanate, cycloaliphatic diisocyanate, or a linear or branched acyclic aliphatic diisocyanate,
the weight percentages being expressed relative to the total weight of the polyurethane composition, said process, comprising a step in which the compound or compounds A and other ingredient or ingredients optionally present in said composition, are mixed with a polyurethane composition comprising at least one polyurethane bearing NCO end groups based on MDI, which is not solid at a temperature ranging from 5 to 35° C., and a MDI content of less than or equal to 1% by weight relative to the weight of said polyurethane composition, at a temperature of less than or equal to 50° C., under anhydrous conditions in post-synthesis of said MDI-based polyurethane bearing NCO end groups.