Low dust additives comprising emulsified powder for joint compounds and joint compounds thereof
The present invention relates generally to wall repair compounds such as joint compounds, spackling compounds, and the like used to repair imperfections in walls or fill joints between adjacent wallboard panels. Particularly, the present invention relates to such a wall repair compound comprising a dust reduction additive that reduces the quantity of airborne dust generated when the hardened compound is sanded and also exhibits improved adhesive properties. The dust reduction additive also imparts adhesion to the wall repair compounds to which it is added, for example to a joint compound. The dust reduction additive is a powder prepared from colloidally-protected, wax-based microstructure dispersions.
1. A low-dust joint compound composition comprising a dust reduction additive emulsified powder, wherein said dust reduction additive emulsified powder is made from an emulsion comprising a colloidally-protected-waxed-based (CPWB) microstructure comprising:
(A) a wax core,
wherein said wax core comprises a micro-crystalline wax component, a non-micro-crystalline wax component, or a combination thereof,
wherein said micro-crystalline wax component comprises at least one linear alkane wax defined by the general formula C n H 2n+2 , where n ranges from 13-80,
wherein said non-micro-crystalline wax component comprises at least one wax selected from the group consisting of animal-based wax, plant-based wax, mineral wax, synthetic wax, a wax containing organic acids and/or esters, anhydrides, an emulsifier containing a mixture of organic acids and/or esters, and combinations thereof; and
(B) a polymeric shell,
wherein said polymeric shell comprises at least one polymer selected from the group consisting of polyvinyl alcohol, polyvinyl alcohol copolymers, polyvinyl alcohol terpolymers, polyvinyl acetate, polyvinyl acetate copolymers, polyvinyl acetate terpolymers, cellulose ethers, polyethylene oxide, polyethyleneimines, polyvinylpyrrolidone, polyvinylpyrrolidone copolymers, polyethylene glycol, polyacrylamides polyethylene glycol, polyacrylamides and poly(N-iso-propylamides), pullulan, sodium alginate, gelatin, starches, and combinations thereof.
2. The low-dust joint compound composition as recited in claim 1 , wherein the composition further comprises at least one component selected from the group consisting of a filler; a binder; a thickener; a non-leveling agent' a preservative; a rheology modifier; and a surfactant.
3. The low-dust joint compound composition as recited in claim 1 , wherein:
said filler is selected from the group consisting of calcium carbonate (CaCO 3 ), calcium sulfate dihydrate (CaSO 4 2H 2 O), calcium sulfate hemihydrate (CaSO 4 -1/2H 2 O), glass micro bubbles, mica, perlite, talc, limestone, pyrophyllite, silica, diatomaceous earth, cristobalite, a micro-roughened filler, clay, and combinations thereof;
said binder is selected from the group consisting of polyvinyl acetate, polyvinyl alcohol, ethylene vinyl acetate co-polymer, vinylacrylic copolymer, styrene-butadiene, polyacrylamide, acrylic polymers, latex, natural starch, synthetic starch, casein, and combinations thereof;
said thickener is selected from the group consisting of methyl cellulose, hydroxypropyl cellulose, hydroxypropyl methyl cellulose, hydroxyethyl cellulose, hydroxyethyl methyl cellulose, hydroxyethyl hydroxypropyl cellulose, ethylhydroxethyl cellulose, sodium carboxymethyl cellulose, and combinations thereof; and
said non-leveling agent is selected from the group consisting of attapulgite clay, bentonite, illite, kaolin, sepiolite, clays mixed with starches, and combinations thereof.
4. The low-dust joint compound composition as recited in claim 1 , wherein the weight of said dust reduction additive emulsified powder is in the range of from about 0.1% to about 20% by weight of said low-dust joint compound composition.
5. The low-dust joint compound composition as recited in claim 3 , wherein the weight of said dust reduction additive emulsified powder is in the range of from about 0.1% to about 10% by weight of said low-dust joint compound composition.
6. The low-dust joint compound composition as recited in claim 1 , wherein the peak air-borne dust generation of said low-dust joint compound composition is less than 100 mg/m 3 .
7. The low-dust joint compound composition as recited in claim 1 , wherein the composition further comprises at least one component from a silicone, a siliconate, a fluorinated compound, a stearate, or a combination thereof.
8. The low-dust joint compound composition of claim 7 , wherein the silicone, siliconate, fluorinated compound, or stearate is selected from the group consisting of metal siliconate salts, potassium siliconate, poly hydrogen methyl siloxane, polydimethyl siloxane, stearate-based salts, and combinations thereof.