Dry animal-derived collagen fiber tissue material and preparation method and bioprothesis thereof
A dry animal-derived collagen fiber tissue material and preparation method and bioprosthesis thereof are disclosed. The preparation method includes: 1) rinsing of an animal-derived collagen fiber tissue material that has been treated with a crosslinking agent; 2) immersion of the rinsed tissue material in a non-aqueous alcoholic solution for dehydration; 3) successive immersion of the tissue material that has been dehydrated with the non-aqueous alcoholic solution in saccharide solutions of different gradients of concentrations for gradient dehydration; 4) taking out and drying of the gradient dehydrated tissue material; and 5) hermetic packaging of the dried tissue material and sterilization. The preparation method is simple and allows the use of easily-available low-cost materials, resulting in lower costs. In addition, it can reduce the toxicity caused by a residue of the aldehyde crosslinking agent. The prepared biological tissue material is pliable and tough, less prone to bending or warping, has a water content that can be well controlled and better biocompatibility due to absence of polyhydric alcohol residues.
1. A preparation method of a dry animal-derived collagen fiber tissue material, comprising:
1) rinsing an animal-derived collagen fiber tissue material that has been treated with a crosslinking agent;
2) immersing the rinsed tissue material in a non-aqueous alcoholic solution for dehydration;
3) successively immersing the tissue material that has been dehydrated with the non-aqueous alcoholic solution in saccharide solutions of different gradients of concentrations for gradient dehydration;
4) taking out and drying of the gradient dehydrated tissue material; and
5) hermetic packaging of the dried tissue material and sterilizing the dried tissue material.
2. The preparation method of claim 1 , wherein the biological tissue material is pericardium, heart valves, peritoneum, pleura, small intestinal submucosa, dura mater, spinal dura, ligaments or skin.
3. The preparation method of claim 1 , wherein the crosslinking agent in step 1) is one or more of glutaraldehyde, genipin, procyanidins and carbodiimide.
4. The preparation method of claim 1 , wherein the rinsing in step 1) is accomplished by shaking at 50-150 rpm for 3-60 minutes at 4-25° C. in a isotonic solution containing 5%-30% (v/v) of isopropanol and/or ethanol.
5. The preparation method of claim 4 , wherein the isotonic solution is a normal saline solution, or a phosphate buffer solution having a pH of 6.8-8.6, or a D-Hanks buffer solution having a pH of 6.8-8.6.
6. The preparation method of claim 1 , wherein the non-aqueous alcoholic solution in step 2) is a solution of aliphatic alcohol(s) with each aliphatic alcohol having a molecular weight of less than 1000D.
7. The preparation method of claim 6 , wherein the non-aqueous alcoholic solution is a solution of a polyether diol and/or a C2-C6 aliphatic alcohol.
8. The preparation method of claim 7 , wherein the non-aqueous alcoholic solution contains polyethylene glycol or glycerol accounting for 20%-90% by volume or contains polyethylene glycol and glycerol together accounting for 20%-90% by volume.
9. The preparation method of claim 6 , wherein the non-aqueous alcoholic solution is a solution of one or more of polyethylene glycol, triethylene glycol, 1,2,6-hexanetriol, 1,2,4-butanetriol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, glycerol, isopropanol and ethanol.
10. The preparation method of claim 9 , wherein the polyethylene glycol has a number-average molecular weight of 200-1000.
11. The preparation method of claim 1 , wherein in step 2), the rinsed tissue material is immersed for 30 minutes to 24 hours in a dark condition at 20-37° C.
12. The preparation method of claim 1 , wherein each of the saccharide solutions in step 3) is a solution of a moisturizing monosaccharide, disaccharide, trisaccharide, polysaccharide or sugar alcohol that can absorb moisture.
13. The preparation method of claim 12 , wherein each of the saccharide solutions is a solution of fructose, saccharose, trehalose, non-crystalline raffinose, chitosan, a chitosan-modified polysaccharide, sorbitol or mannitol.
14. The preparation method of claim 1 , wherein the gradient dehydration in step 3) is accomplished by immersing the tissue material that has been dehydrated with the non-aqueous alcoholic solution successively in each of the saccharide solutions of different gradients of concentrations at 4-37° C. in a dark condition for 5 minutes to 48 hours.
15. The preparation method of claim 1 , wherein the saccharide solutions of different gradients of concentrations in step 3) are respectively 30%, 40%, 50%, 55%, 60% and 65% (w/v) aqueous saccharose solutions or 50%, 60%, 70%, 75%, 80% and 85% (w/v) aqueous solutions of fructose, trehalose, non-crystalline raffinose, chitosan, chitosan-modified polysaccharide, sorbitol or mannitol.
16. The preparation method of claim 1 , wherein in step 4), the gradient dehydrated tissue material is taken out and dried by using a fibrous desiccant or by placing the gradient dehydrated tissue material in a dark condition at 20° C.-37° C. for 10 minutes to 24 hours.
17. The preparation method of claim 16 , wherein the fibrous desiccant is selected from the group consisting of raw sheets, folded sheets, sheets in bags, columns and lamination.
18. The preparation method of claim 1 , wherein the hermetic packaging is accomplished by hermetically sealing the dried tissue material in a packaging container in an environment with a relative humidity of less than 30% or in an inert environment.