Methods of nanostructure formation and shape selection
Methods for forming nanostructures of various shapes are disclosed. Nanocubes, nanowires, nanopyramids and multiply twinned particles of silver may by formed by combining a solution of silver nitrate in ethylene glycol with a solution of poly(vinyl pyrrolidone) in ethylene glycol. Hollow nanostructures may be formed by reacting a solution of solid nanostructures comprising one of a first metal and a first metal alloy with a metal salt that can be reduced by the first metal or first metal alloy. Nanostructures comprising a core with at least one nanoshell may be formed by plating a nanostructure and reacting the plating with a metal salt.
1. A method of manufacturing metal nanostructures, the method comprising:
preparing a mixture comprising a metal salt, a polyol, and a capping agent under a set of reaction conditions,
wherein the set of reaction conditions yields a desired nanostructure shape at a higher percentage than other nanostructure shapes, the set of reaction conditions comprising a concentration of a metal salt in a polyol and a molar ratio of the capping agent to the metal salt, and
wherein the desired nanostructure shape is selected from one of nanocubes, half-cubes, pyramids, nanowires, and multiply-twinned particles;
allowing the mixture to react under the set of reaction conditions to form metal nanostructures; and
separating the metal nanostructures having the desired nanostructure shape from metal nanostructures having other nanostructure shapes.
2. The method of claim 1 , wherein the metal salt is a silver salt.
3. The method of claim 1 , wherein the metal salt is silver nitrate.
4. The method of claim 1 , wherein the capping agent is poly(vinyl pyrrolidone) (PVP).
5. The method of claim 1 , wherein the polyol is ethylene glycol.
6. A method of manufacturing metal nanostructures, the method comprising:
preparing a mixture comprising a metal salt, a polyol, and a capping agent under a set of reaction conditions,
wherein the set of reaction conditions yields a desired nanostructure shape at a higher percentage than other nanostructure shapes, the set of reaction conditions comprising a concentration of a metal salt in a polyol and a molar ratio of the capping agent to the metal salt,
wherein the desired nanostructure shape is nanowires, and
wherein the concentration of the metal salt in the polyol is less than 0.1 mol/dm 3 ;
allowing the mixture to react under the set of reaction conditions to form metal nanostructures; and
separating metal nanowires from metal nanostructures having other nanostructure shapes.