Adsorbent for adsorbing iodine compounds and/or antimony, method for preparing said adsorbent, and method and apparatus for treating radioactive waste liquid by using said absorbent
Provided are an adsorbent capable of removing radioactive water liquid including iodine compounds and/or antimony by means of a water passing treatment, and a method and an apparatus for treating radioactive waste liquid by using the adsorbent. The adsorbent includes a polymer resin and 10 parts by weight or more of a hydrous hydroxide of a rare earth element based on 100 parts by weight of the polymer resin, in which the hydrous hydroxide of the rare earth element has a water content of 1 part by weight to 30 parts by weight based on 100 parts by weight of a dry product thereof, and adsorbs iodine compounds and/or antimony.
1. An adsorbent comprising:
a polymer resin; and
10 parts by weight or more of a hydrous hydroxide of a rare earth element based on 100 parts by weight of the polymer resin,
wherein the hydrous hydroxide of the rare earth element has a water content of 1 part by weight to 30 parts by weight based on 100 parts by weight of a dry product thereof, and adsorbs iodine compounds and/or antimony.
2. The adsorbent of claim 1 , wherein the adsorbent has an average particle diameter of 0.2 mm to 5.0 mm.
3. The adsorbent of wherein the hydrous hydroxide of the rare earth element is an aggregate whose secondary particles have an average particle diameter of 0.2 μm to 25 μm.
4. The adsorbent of claim 1 , wherein the polymer resin is a fluorine-based resin or a polyvinyl-based resin, and
the rare earth element constituting the hydrous hydroxide of the rare earth element is selected from scandium (Sc), yttrium (Y), a lanthanoid element, lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), lutetium (Lu), and a combination thereof.
5. The adsorbent of claim 4 , wherein the hydrous hydroxide of the rare earth element is cerium hydroxide (IV).n-hydrate (Ce(OH)4.nH2O).
6. The adsorbent of claim 1 , wherein a content of the hydrous hydroxide of the rare earth element is 400 parts by weight or more based on 100 parts by weight of the polymer resin.
7. The adsorbent of claim 1 , further comprising 10 parts by weight or more of silver zeolite based on 100 parts by weight of the polymer resin.
8. The adsorbent of claim 7 , wherein the silver zeolite is an aggregate having an average particle diameter of 1 μm to 10 μm, which is formed by supporting silver onto a zeolite selected from A-type, X-type, Y-type,β-type, mordenite-type, chabazite-type, or a combination of one or more thereof.
9. A method for treating radioactive waste liquid, comprising adsorbing and removing iodine compounds and/or antimony by allowing the radioactive waste liquid to pass through an adsorption tower filled with the adsorbent of claim 1 with a layer height of 10 cm to 300 cm at a water passing linear velocity (LV) of 1 m/h to 40 m/h and a space velocity (SV) of 200 h-1 or less.
10. An apparatus for treating radioactive waste liquid, comprising an adsorption tower filled with the adsorbent of claim 1 with a layer height of 10 cm to 300 cm.