Electrically charged nonwoven fabric, filtration material including same, and method for producing electrically charged nonwoven fabric
Use of an electrically charged nonwoven fabric that is made of a fiber predominantly composed of an amorphous polymer provides a novel filtration material having improved performance compared to that of conventional filtration materials, and having excellent heat resistance and excellent flame retardancy as well as an electrically charged nonwoven fabric for use in the filtration material. It is preferable that the surface charge density is greater than or equal to 1×10 −10 coulomb/cm 2 . It is preferable that the collection efficiency for collecting a dust particle with a particle diameter of 1 μm flowing at a fabric-passing velocity of 8.6 cm/second is greater than or equal to 40%, the QF value is greater than or equal to 0.05, and the decrement of the dust-particle collection efficiency after being allowed to leave at 100° C. for 24 hours is less than or equal to 10%.
1. An electrically charged nonwoven fabric comprising a fiber predominantly comprising an amorphous polymer, wherein a QF value of the electrically charged nonwoven fabric is greater than or equal to 0.1.
2. The electrically charged nonwoven fabric according to claim 1 , wherein the electrically charged nonwoven fabric has a surface charge density of greater than or equal to 1×10 −10 coulomb/cm 2 .
3. The electrically charged nonwoven fabric according to claim 1 , wherein the electrically charged nonwoven fabric has a collection efficiency for collecting a dust particle with a particle diameter of 1 μm flowing at a fabric-passing velocity of 8.6 cm/second of greater than or equal to 40%.
4. The electrically charged nonwoven fabric according to claim 3 , wherein the decrement of the dust-particle collection efficiency after being allowed to leave at 100° C. for 24 hours is less than or equal to 20%.
5. The electrically charged nonwoven fabric according to claim 1 , wherein the amorphous polymer has a glass transition temperature of greater than or equal to 200° C.
6. The electrically charged nonwoven fabric according to claim 1 , wherein the amorphous polymer is an amorphous polyetherimide.
7. The electrically charged nonwoven fabric according to claim 6 , wherein a weight average molecular weight (Mw) of the amorphous polyetherimide is from 1000 to 80000.
8. The electrically charged nonwoven fabric according to claim 6 , wherein a weight average molecular weight (Mw) of the amorphous polyetherimide is from 2000 to 50000.
9. The electrically charged nonwoven fabric according to claim 6 , wherein a weight average molecular weight (Mw) of the amorphous polyetherimide is from 3000 to 40000.
10. The electrically charged nonwoven fabric according to claim 6 , wherein the amorphous polyetherimide is a condensate of 2,2-bis[4-(2,3-dicarboxyphenoxy)phenyl]propane dianhydride and m-phenylenediamine or p-phenylenediamine.
11. The electrically charged nonwoven fabric according to claim 6 , wherein the fiber has an average fiber diameter from 1 to 25 μm.
12. The electrically charged nonwoven fabric according to claim 1 , wherein the electrically charged nonwoven fabric has a thickness within a range from 10 to 1000 μm.
13. The electrically charged nonwoven fabric according to claim 1 , produced by a melt blown method or a spunbonding method.
14. The electrically charged nonwoven fabric according to claim 13 , wherein electrical charging is conducted by a corona discharge method, a hydro-charging method, or both.
15. A filtration material comprising the electrically charged nonwoven fabric according to claim 1 .
16. A method for producing an electrically charged nonwoven fabric, comprising:
forming a nonwoven fabric by a melt blown method or a spunbonding method using a fiber predominantly comprising an amorphous polymer; and
electrically charging the resulting nonwoven fabric by a corona discharge method, a hydro-charging method, or both.