Polyester film containing furandicarboxylate unit
To provide a furandicarboxylate unit-containing polyester film usable for industrial and packaging purposes. The film of the present invention is a polyester film, which is a biaxially oriented film of a polyester resin including a dicarboxylic acid component containing mainly a furandicarboxylic acid and a glycol component containing mainly ethylene glycol, wherein the film has a plane orientation coefficient ΔP of not less than 0.005 and not more than 0.200 and a film thickness of not thinner than 1 micro meter and not thicker than 300 micro meters.
1. A polyester film, which is a biaxially oriented film of a polyester resin comprising a dicarboxylic acid component containing mainly a furandicarboxylic acid and a glycol component containing mainly ethylene glycol,
wherein the film has
a plane orientation coefficient ΔP of 0.100 or more and 0.160 or less,
a thickness of 5 μm or more and 200 μm or less, and
a heat shrinkage rate of not less than 0.01% and not more than 30% when heated at 150° C. for 30 minutes in a machine direction of film plane and in a transverse direction perpendicular to the machine direction.
2. The polyester film according to claim 1 , wherein the polyester film has a heat shrinkage rate of not less than 0.01% and not more than 20% when heated at 150° C. for 30 minutes.
3. The polyester film according to claim 2 , wherein the polyester film has an oxygen permeability of not less than 1 mL/m 2 /day/MPa and not more than 200 mL/m 2 /day/MPa per 50 micro meters of film thickness under a temperature of 23° C. and a humidity of 65%.
4. The polyester film according to claim 3 , wherein the polyester film has a refractive index of not less than 1.5700 and not more than 1.7000 in a machine direction of film plane (nx) and in a transverse direction perpendicular to the machine direction (ny).
5. The polyester film according to claim 4 , wherein the polyester film has a heat shrinkage rate of not less than 0.01% and not more than 10% when heated at 150° C. for 30 minutes.
6. The polyester film according to claim 5 , wherein the polyester film has a heat shrinkage rate of not less than 0.01% and not more than 8% when heated at 150° C. for 30 minutes.
7. The polyester film according to claim 6 , wherein the polyester film has a heat shrinkage rate of not less than 0.01% and not more than 4.5% when heated at 150° C. for 30 minutes.
8. The polyester film according to claim 7 , wherein the polyester film has a plane orientation coefficient ΔP of not less than 0.100 and not more than 0.200.
9. A method for producing the polyester film according to claim 8 , comprising a stretching process for stretching an unstretched film in the machine direction and in the direction perpendicular to the machine direction to obtain a stretched film, and a relaxation process for relaxing the stretched film.
10. The polyester film according to claim 1 , wherein the polyester film has an oxygen permeability of not less than 1 mL/m 2 /day/MPa and not more than 200 mL/m 2 /day/MPa per 50 micro meters of film thickness under a temperature of 23° C. and a humidity of 65%.
11. The polyester film according to claim 1 , wherein the polyester film has a refractive index of not less than 1.5700 and not more than 1.7000 in a machine direction of film plane (nx) and in a transverse direction perpendicular to the machine direction (ny).
12. The polyester film according to claim 1 , wherein the polyester film has a heat shrinkage rate of not less than 0.01% and not more than 10% when heated at 150° C. for 30 minutes.
13. The polyester film according to claim 1 , wherein the polyester film has a plane orientation coefficient ΔP of not less than 0.100 and not more than 0.200.
14. A method for producing the polyester film according to claim 1 , comprising a stretching process for stretching an unstretched film in the machine direction and in the direction perpendicular to the machine direction to obtain a stretched film, and a relaxation process for relaxing the stretched film.