Moisture barriers for paper materials
Provided herein is a tobacco packaging material, comprising a paper material coated with at least one polymer layer. The polymer layer comprises at least one repulpable polymer, and wherein the tobacco packaging material has a water vapor transmission rate (WVTR) that is at least 90% lower than the paper material. Further provided is a tobacco package comprising the tobacco packaging material, wherein the tobacco package is substantially free of any foil inner liner or polypropylene film. Further described is a method for making the tobacco packaging material, comprising extrusion coating at least one repulpable polymer onto a paper material to form a polymer layer, and optionally further depositing at least one atomic layer deposition (ALD) layer that comprises a metal oxide.
1. A tobacco packaging material, comprising:
a paper material coated with at least one polymer layer, and
at least two atomic layer deposition (ALD) layers comprising at least one inorganic layer comprising a metal oxide and at least one partially organic layer comprising a metal oxide and an elastic organic material coated on the at least one polymer layer, and the at least one inorganic layer coated on the at least one partially organic layer;
wherein the polymer layer comprises at least one repulpable polymer, and
wherein the tobacco packaging material has a water vapor transmission rate (WVTR) that is at least 90% lower than the paper material.
2. The tobacco packaging material of claim 1 , wherein the polymer layer comprises a polymer selected from the group consisting of polyglycolic acid (PGA) and polylactic acid (PLA).
3. The tobacco packaging material of claim 1 , wherein the paper material is coated with at least two polymer layers having different crystallinity from each other.
4. The tobacco packaging material of claim 1 , wherein the paper material is coated with about 1-100 g/m 2 of the repulpable polymer.
5. The tobacco packaging material of claim 1 , wherein the metal oxide is selected from the group consisting of Al 2 O 3 and SiO 2 .
6. The tobacco packaging material of claim 1 , wherein the tobacco packaging material has a WVTR of 10 g/m 2 /day or less at 38° C. and 90% RH.
7. The tobacco packaging material of claim 1 , wherein the tobacco packaging material has a WVTR of 3.4 g/m 2 /day or less at 38° C. and 90% RH.
8. A tobacco package comprising the tobacco packaging material of claim 1 , wherein the tobacco package is substantially free of any foil inner liner or polypropylene film.