Thermal and environmental barrier coating compositions and methods of deposition
A coated substrate is provided that comprises: a substrate; and a barrier coating comprising a compound having the formula: Ln 2 ABO s , where Ln comprises scandium, yttrium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, or mixtures thereof; A comprises Si, Ti, Ge, Sn, Ce, Hf, Zr, or a combination thereof; and B comprises Mo, W, or a combination thereof. In one embodiment, B comprises Mo.
1. A coated substrate, comprising:
a substrate, wherein the substrate comprises a ceramic matrix composite; and
a barrier coating comprising a compound having the formula:
Ln 2 ABO 8
where Ln comprises scandium, yttrium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, or mixtures thereof;
A comprises Si, Ti, Ge, Sn, Ce, Hf, Zr, or a combination thereof; and
B comprises Mo, W, or a combination thereof.
2. The coated substrate as in claim 1 , wherein Ln is selected from the group consisting of scandium (Sc), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), lutetium (Lu), and mixtures thereof.
3. The coated substrate as in claim 1 , wherein Ln comprises yttrium.
4. The coated substrate as in claim 1 , wherein B comprises Mo.
5. The coated substrate as in claim 4 , wherein the compound has the formula:
Ln 2 AMo 8 W 1−x O 8 ,
where 0.1≤x≤0.5.
6. The coated substrate as in claim 1 , wherein B comprises W or a combination of Mo and W.
7. The coated substrate as in claim 6 , wherein the compound has the formula:
Ln 2 AMo x W 1−x O 8
where 0≤x≤0.5.
8. The coated substrate as in claim 7 , wherein A comprises Si.
9. The coated substrate as in claim 8 , wherein the compound has the formula:
Ln 2 Si y A 1−y Mo x W 1−x O 8
where 0≤x≤0.5;
0<y≤0.5; and
A is Ti, Ge, Sn, Ce, Hf, Zr, or a combination thereof.
10. The coated substrate as in claim 1 , wherein the compound has the formula:
Y 2 SiMoO 8 .
11. The coated substrate as in claim 1 , wherein A comprises Hf and/or Zr.
12. The coated substrate as in claim 1 , wherein the compound comprises a zircon crystal structure or a scheelite structure.
13. The coated substrate as in claim 1 , wherein the coated substrate further comprises a bond coat layer positioned between the substrate and the barrier coating.
14. The coated substrate as in claim 13 , wherein the bond coat layer comprises silicon, silicon carbide, silicon nitride, molybdenum silicide, rhenium silicide, or combinations thereof.
15. The coated substrate as in claim 1 , wherein the coated substrate further comprises an outer coat layer on the barrier coating, and wherein the outer coat layer comprises Ln 2 SiO 5 , where Ln is scandium (Sc), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb), lutetium (Lu), or mixtures thereof.
16. The coated substrate as in claim 1 , wherein a mixture of an oxyapetite phase and an Ln 2 AO 5 phase forms on a surface of the barrier coating.
17. The coated substrate as in claim 1 , wherein the barrier coating comprises a a single phase structure with less than 10% by volume of a secondary crystal phase.
18. The coated substrate as in claim 17 , wherein the single phase structure is a zircon crystal structure.
19. The coated substrate as in claim 17 , wherein the single phase structure is a scheelite crystal structure.