Biaxially stretched polypropylene film for capacitor

1. A biaxially stretched polypropylene film for capacitors, obtained by biaxially stretching a polypropylene resin,

the polypropylene film having a crystallite size of 122 Å or less as determined by the Scherrer's equation from the half width of the reflection peak from (040) plane of α-crystal measured by a wide angle X-ray diffraction method, and

the polypropylene film having a value of birefringence ΔNyz with respect to a thickness direction of 7.0×10 −3 or more and 10.0×10 −3 or less as measured by an optical birefringence measurement.

2. The biaxially stretched polypropylene film for capacitors according to claim 1 ,

wherein the polypropylene film has protrusions, and

when a surface shape measurement is carried out on at least one surface of the polypropylene film in a visual field of 240 μm×180 μm by using a light interferometric non-contact surface profiler, the total volume of protrusions having a height of 0.02 μm or more is 10 μm 3 or more and 120 μm 3 or less per visual field.

3. The polypropylene film according to claim 1 , wherein the polypropylene resin contains a polypropylene resin A, and the polypropylene resin A has the following characteristics:

a weight average molecular weight (Mw) of 250,000 or more and 450,000 or less;

a molecular weight distribution (Mw/Mn) of 7.0 or more and 12.0 or less;

a ratio of Z-average molecular weight/number average molecular weight (Mz/Mn) of 20.0 or more and 70.0 or less;

a difference, as obtained by subtracting a differential distribution value when the logarithmic molecular weight Log(M)=6.0 from a differential distribution value when Log(M)=4.5 on a molecular weight distribution curve, of 8.0% or more and 18.0% or less; and

a mesopentad fraction ([mmmm]) of 94.0% or more and less than 98.0%.

4. The polypropylene film according to claim 3 , wherein the polypropylene resin further contains a polypropylene resin B, and the polypropylene resin B has the following characteristics:

a Mw of 300,000 or more and 400,000 or less;

a Mw/Mn of 7.0 or more and 9.0 or less; and

a difference, as obtained by subtracting a differential distribution value when the logarithmic molecular weight Log(M)=6.0 from a differential distribution value when Log(M)=4.5 on a molecular weight distribution curve, of 1.0% or more and less than 8.0%; and

wherein the polypropylene resin B is contained in an amount of 10 wt. % or more and 45 wt. % or less, based on 100 wt. % of the entire polypropylene resin.

5. The polypropylene film according to claim 1 , wherein the polypropylene film contains at least one hindered phenol-based antioxidant having a carbonyl group, and the content of the antioxidant in the film is 4,000 ppm by mass or more and 6,000 ppm by mass or less, based on 100 parts by weight of the polypropylene resin.

6. The polypropylene film according to claim 1 , wherein at least one side of the polypropylene film has a surface roughness such that the center line average roughness (Ra) is 0.03 μm or more and 0.08 μm or less, and the maximum height (Rz) is 0.3 μm or more and 0.8 μm or less.

7. The polypropylene film according to claim 1 , wherein the polypropylene film has a thickness of 1.0 μm or more and 6.0 μm or less.

8. A metallized polypropylene film for capacitors, comprising the biaxially stretched polypropylene film for capacitors according to claim 1 , wherein a metal is deposited on one side or both sides of the polypropylene film.

9. A capacitor produced using the metallized polypropylene film for capacitors according to claim 8 .