Expanded-glass granular material and method for producing same
In a method for producing an expanded-glass granular material, starting materials containing glass powder, water glass, at least one blowing agent, and metakaolin, are mixed in order to form a homogeneous slurry. The slurry is granulated to form raw granular-material particles, which are foamed at a baking temperature between 780° C. and 950° C. in order to form expanded-glass granular-material particles. The expanded-glass granular material has a long-term water absorption of less than 25 volume percent when the expanded-glass granular material is exposed to water for a time period of 21 days.
1. A method for producing expanded glass granules, which comprises the following steps of:
mixing a homogeneous slip from starting materials containing finely ground glass, potassium waterglass, metakaolin, and at least one expandant, the starting materials being mixed for forming the homogeneous slip, based on a total mass of solids contained in the starting materials, containing a metakaolin solids fraction of between 0.5 mass % and 7 mass %;
granulating the homogeneous slip to form crude granular particles; and
foaming the crude granular particles to form expanded glass granular particles at a firing temperature of between 780° C. and 950° C.
2. The method according to claim 1 , wherein the starting materials mixed to form the homogeneous slip, based on a total mass of solids contained in the starting materials, contain:
finely ground glass solids fractions of between 83 mass % and 90 mass %;
waterglass solids fractions of between 7.5 mass % and 11 mass %; and
expandant solids fractions of between 0.8 mass % and 2.5 mass %.
3. The method according to claim 1 , wherein the starting materials mixed to form the homogeneous slip contain the potassium waterglass and sodium waterglass.
4. The method according to claim 3 , wherein the starting materials mixed to form the homogeneous slip, based on a total mass of a solids contained in the starting materials, contain:
potassium waterglass solids fractions of between 7 mass % and 9 mass %; and
sodium waterglass solids fractions of between 1 mass % and 2.5 mass %.
5. The method according to claim 1 , wherein the starting materials mixed to form the homogeneous slip contain sodium nitrate as an expandant.
6. The method according to claim 5 , wherein the starting materials mixed to form the homogeneous slip contains sodium nitrate and glucose as expandants.
7. The method according to claim 6 , wherein the starting materials mixed to form the homogeneous slip, based on a total mass of solids contained in the starting materials, contains:
sodium nitrate solids fractions of between 0.75 mass % and 2.5 mass %; and
glucose solids fractions of between 0.05 mass % and 0.5 mass %.
8. The method according to claim 1 , wherein the starting materials mixed to form the homogeneous slip contain aluminum hydroxide.
9. The method according to claim 8 , wherein the starting materials mixed to form the homogeneous slip, based on the total mass of the solids contained in the starting materials, contain an aluminum hydroxide solids fraction of between 0.25 mass % and 3 mass %.
10. The method according to claim 1 , wherein the starting materials mixed to form the homogeneous slip, based on a total mass of solids contained in the starting materials, contain a metakaolin solids fraction of between 1.0 mass % and 5 mass %.
11. The method according to claim 1 , wherein the starting materials mixed to form the homogeneous slip, based on a total mass of solids contained in the starting materials, contain:
finely ground glass solids fractions of between 85.3 mass % and 88.9 mass %;
waterglass solids fractions of between 8.1 mass % and 10.5 mass %; and
expandant solids fractions of between 1.0 mass % and 2.3 mass %.
12. The method according to claim 3 , wherein the starting materials mixed to form the homogeneous slip, based on a total mass of a solids contained in the starting materials, contain:
potassium waterglass solids fractions of between 6.8 mass % and 8.4 mass %; and
sodium waterglass solids fractions of between 1.3 mass % and 2.1 mass %.
13. The method according to claim 6 , wherein the starting materials mixed to form the homogeneous slip, based on a total mass of solids contained in the starting materials, contains:
sodium nitrate solids fractions of between 1.0 mass % and 2.2 mass %; and
glucose solids fractions of between 0.06 mass % and 0.16 mass %.
14. Expanded glass granules, comprising:
a homogeneous slip containing starting materials including finely ground glass, potassium waterglass, metakaolin, and at least one expandant, said starting materials mixed for forming said homogeneous slip, based on a total mass of solids contained in said starting materials, containing a metakaolin solids fraction of between 0.5 mass % and 7 mass %;
the homogeneous slip being granulated to form crude granular particles, the crude granular particles being foamed to form expanded glass granular particles at a firing temperature of between 780° C. and 950° C.; and
the expanded glass granules having a long-term water absorption of less than 15 volume percent when exposed to water for a period of 21 days.
15. The expanded glass granules according to claim 14 , wherein the expanded glass granules have an apparent particle density of less than 900 kg/m 3 .