Liner-type, antistatic topcoat system for aircraft canopies and windshields
A coated substrate includes: a substrate; an electrically conductive multilayer stack on the substrate; and a coating on the electrically conductive multilayer stack. A thickness of the coating is 5 to 10 mils and the coating includes a conductive, anti-static tiecoat on the electrically conductive multilayer stack; and a conductive, anti-static topcoat on the conductive, anti-static tiecoat. The conductive, anti-static tiecoat and the conductive, anti-static topcoat are formed from a coating composition including a hydrophobic first aliphatic polyisocyanate, a second aliphatic polyisocyanate including a hydrophilic portion, a polyester polyol, a hydrophilic polyol, and a fluorinated polyol compound is disclosed.
1. A coated substrate comprising:
a substrate;
an electrically conductive multilayer stack on the substrate; and
a coating on the electrically conductive multilayer stack, a thickness of the coating being 5 to 10 mils and the coating comprising:
a conductive, anti-static tiecoat on the electrically conductive multilayer stack; and
a conductive, anti-static topcoat on the conductive, anti-static tiecoat, and
the conductive, anti-static tiecoat being formed from a coating composition comprising a hydrophobic first aliphatic polyisocyanate, a second aliphatic polyisocyanate comprising a hydrophilic portion, a polyester polyol, a hydrophilic polyol, and a fluorinated polyol.
2. The coated substrate of claim 1 , wherein a thickness of each of the conductive, anti-static topcoat and the conductive, anti-static tiecoat is 2.5 to 5 mils.
3. The coated substrate of claim 1 , wherein the thickness of the coating is 5 to 8 mils.
4. The coated substrate of claim 3 , wherein a thickness of each of the conductive, anti-static topcoat and the conductive, anti-static tiecoat is 2.5 to 4 mils.
5. The coated substrate of claim 1 , wherein the thickness of the coating is 6 to 8 mils.
6. The coated substrate of claim 5 , wherein a thickness of each of the conductive, anti-static topcoat and the conductive, anti-static tiecoat is 3 to 4 mils.
7. The coated substrate of claim 1 , wherein a thickness of the conductive, anti-static tiecoat is at least 3 mils.
8. The coated substrate of claim 1 , wherein a thickness of the conductive, anti-static topcoat is at least 3 mils.
9. The coated substrate of claim 1 , wherein the conductive, anti-static tiecoat is substantially free of inherently conductive polymers, ionic liquids, conductive oxides and carbon nanotubes.
10. The coated substrate of claim 1 , wherein the conductive, anti-static topcoat is substantially free of inherently conductive polymers, ionic liquids, conductive oxides and carbon nanotubes.
11. The coated substrate of claim 1 , further comprising a tiecoat between the substrate and the electrically conductive multilayer stack.
12. The coated substrate of claim 11 , further comprising a basecoat between the tiecoat and the electrically conductive multilayer stack.
13. The coated substrate of claim 1 , further comprising a primer layer between the electrically conductive multilayer stack and the conductive, anti-static tiecoat.
14. The coated substrate of claim 1 , wherein the coating has a resilience such that the coating can be stretched to a length 50% or more longer than the as-formed length of the coating substantially without tearing the coating.
15. The coated substrate of claim 1 , wherein the coating has a resilience such that the coating can be stretched to a length 100% or more longer than the as-formed length of the coating substantially without tearing the coating.
16. The coated substrate of claim 1 , wherein the coating has a resilience such that the coating can be stretched to a length 200% or more longer than the as-formed length of the coating substantially without tearing the coating.
17. The coated substrate of claim 1 , wherein the second aliphatic polyisocyanate further comprises a hydrophobic portion.
18. The coated substrate of claim 17 , wherein the hydrophobic portion of the second aliphatic polyisocyanate comprises an isophorone diisocyanate moiety or a derivative thereof.
19. The coated substrate of claim 1 , wherein the hydrophilic portion of the second aliphatic polyisocyanate comprises a polyether chain.
20. The coated substrate of claim 1 , wherein the second aliphatic polyisocyanate comprises a polyether chain bonded to an isophorone diisocyanate trimer.