Bicycle saddle manufacturing method
A bicycle saddle manufacturing method includes the steps of expanding a foamable material to form the foamable material into a semi-finished saddle body, and performing a thermoforming process to form the semi-finished saddle body into a saddle in a forming mold. As a result, the bicycle saddle manufacturing method of the present invention can avoid waste of material and environmental pollution.
1. A bicycle saddle manufacturing method comprising the steps of:
a) preparing a preforming mold with a closed chamber;
b) disposing an ethylene-vinyl acetate (EVA) material in the closed chamber of the preforming mold, heating the EVA material to 165° C. and keeping it at the temperature for 15 minutes and then cooling down to the room temperature to form the EVA material into a semi-finished saddle body;
c) preparing a forming mold, the forming mold including an upper die and a lower die, the upper die having a bottom surface, and a protrusion protruded from the bottom surface, the lower die having a top surface, and a cavity concaved from the top surface;
d) removing the semi-finished saddle body from the preforming mold and putting the semi-finished saddle body into the cavity of the forming mold;
e) arranging a woven cloth to cover the semi-finished saddle body and pressing the upper die on the top surface of the lower die to cover the woven cloth on the semi-finished saddle body; and
f) heating up the forming mold 150° C. to a softening temperature of the semi-finished saddle body and keeping it at the temperature for 150-180 seconds to soften the semi-finished saddle body to permeate into the small holes of the woven cloth and to re-expand the semi-finished saddle body to form into a saddle shaped as the shape defined by the protrusion and the cavity.
2. The bicycle saddle manufacturing method as claimed in claim 1 , wherein the EVA material used in the step b) is made by injection molding.
3. The bicycle saddle manufacturing method as claimed in claim 1 , wherein the EVA material used in the step b) is cut from an EVA board which is not yet expanded.
4. The bicycle saddle manufacturing method as claimed in claim 1 , wherein the EVA material disposed in the closed chamber of the preforming mold in the step b) is an EVA sheet which is not yet expanded.
5. The bicycle saddle manufacturing method as claimed in claim 1 , wherein the forming mold further comprises a pressing frame rotatably connected with the upper die and the lower die, and in the step c) further comprises pressing the pressing frame on the top surface of the lower die with a cover cloth disposed therebetween, the cover cloth being positioned on the top surface by the pressing frame and partially located in the cavity.