Surface treatment composition for coated steel sheet, surface treated plated steel sheet and method of production of same, and coated plated steel sheet and method of production of same
An aqueous surface treatment composition for coated steel sheet securing sufficient working adhesion while causing the formation of a surface treatment layer imparting excellent overhang corrosion resistance even without containing chrome, that is, a surface treatment composition containing a specific organic silicon compound, hexafluorometallic acid, a urethane resin having specific cationic groups, a vanadium compound, and an aqueous medium and sufficiently securing working adhesion while imparting excellent overhang corrosion resistance by the urethane resin having cationic groups and a total amine value of specific values is provided.
1. A surface treatment composition for coated steel sheet comprising:
an organic silicon compound (A),
a hexafluorometallic acid (B),
a urethane resin having one or more cationic groups (C),
a vanadium compound (D), and
an aqueous medium (E), wherein
the organic silicon compound (A) is selected from a hydrolyzed product and a hydrolyzed condensate of an aminosilane compound having one or more primary amino groups, as well as mixtures thereof,
the cationic groups of the urethane resin (C) are cationic groups represented by the following general formula [I]:
Wherein each of R 1 , R 2 and R 3 represents, mutually independently, C 1 to C 6 alkyl group or C 2 to C 10 alkylene group, R 4 represents a hydrogen atom or C 1 to C 6 alkyl group, and X − represents an anionic counter ion,
the cationic groups are included in the urethane resin (C) within the range of 0.03 to 0.15 mol/kg, and a total amine value of said urethane resin (C) is 1 to 10 mgKOH/g.
2. The surface treatment composition for coated steel sheet according to claim 1 , wherein
a ratio [MF 6 /NH 2 ] of number of moles of the hexafluorometallic acid (MF 6 ) (B) to a number of moles of the primary amino groups (NH 2 ) of the organic silicon compound (A) is 0.2 to 0.4, and
a solid content mass ratio [(A+B)/C] of the total of the organic silicon compound (A) and the hexafluorometallic acid (B) to the urethane resin (C) is 1.0 to 5.0.
3. The surface treatment composition for coated steel sheet according to claim 1 or 2 , wherein the urethane resin (C) has polycarbonate structural units and polyether structural units.
4. The surface treatment composition for coated steel sheet according to claim 1 or 2 , wherein said hexafluorometallic acid (B) is selected from hexafluorozirconic acid, hexafluorotitanic acid, and mixtures thereof.
5. A surface-treated plated steel sheet comprising plated steel sheet on at least one surface of which is provided a surface treatment layer having film mass of 0.01 to 0.5 g/m 2 formed by coating the plated steel sheet with the surface treatment composition for coated steel sheet according to claim 1 or 2 , then drying the surface treatment composition.
6. The surface-treated steel sheet according to claim 5 , wherein the plated steel sheet is selected from hot dip zinc alloy-plated steel sheet containing, by mass % 55% of Al and 1.6% of Si; Zn—Al—Mg—Si—Cr—Ca(Sr) alloy plated steel sheet with a plating layer comprised of, by mass %, Al: 25 to 75%, Mg: 0.1 to 10%, Si: 1 to 7.5%, Cr: 0.05 to 5.0%, and at least one of Ca and Sr: 0.001 to 0.5%, and having a balance of Zn and unavoidable impurities; and Zn—Al—Mg—Si alloy plated steel sheet with a plating layer comprised of, by mass %, Al: 2 to 19%, Mg: 1 to 10%, and Si: 0.01 to 2%, and having a balance of Zn and unavoidable impurities.
7. A coated plated steel sheet comprising plated steel sheet on at least one surface of which are provided, in order,
a surface treatment layer which includes the surface treatment composition for coated steel sheet according to claim 1 or 2 ,
a primer layer, and
a top layer which contains a colored pigment,
wherein
the primer layer contains a resin having one or more functional groups which can react with the primary amino groups of the organic silicon compound (A) and has a rust-proofing pigment.
8. The coated plated steel sheet according to claim 7 , wherein the plated steel sheet is selected from hot dip zinc alloy-plated steel sheet containing, by mass %, 55% of Al and 1.6% of Si; Zn—Al—Mg—Si—Cr—Ca(Sr) alloy plated steel sheet with a plating layer comprised of, by mass %, Al: 25 to 75%, Mg: 0.1 to 10%, Si: 1 to 7.5%, Cr: 0.05 to 5.0%, and at least one of Ca and Sr: 0.001 to 0.5%, and having a balance of Zn and unavoidable impurities; and Zn—Al—Mg—Si alloy-plated steel sheet with a plating layer comprised of, by mass %, Al: 2 to 19%, Mg: 1 to 10%, and Si: 0.01 to 2%, and having a balance of Zn and unavoidable impurities.
9. A method for producing a surface-treated plated steel sheet, the method comprising a surface treatment step that comprises
coating the surface treatment composition for coated steel sheet according to claim 1 or 2 on at least one surface of the plated steel sheet, and
heating and drying the surface treatment composition to form a surface treatment layer on the surface of the plated steel sheet, without rinsing.
10. The method according to claim 9 , wherein the method further comprises, after the surface treatment step,
a step of coating a primer composition on the surface-treated plated steel sheet and heating and drying the primer composition to form a primer layer, and
a step of applying a top coating composition on the primer layer, then heating and drying the top coating composition to form a top layer.