Lithium manganese composite oxide, secondary battery, electronic device, and method for forming layer
To increase the volume density or weight density of lithium ions that can be received and released in and from a positive electrode active material to achieve high capacity and high energy density of a secondary battery. A lithium manganese composite oxide represented by Li x Mn y M z O w that includes a region belonging to a space group C2/c and is covered with a carbon-containing layer is used as the positive electrode active material. The element M is an element other than lithium and manganese. The lithium manganese composite oxide has high structural stability and high capacity.
1. A method for forming an electrode material, comprising the steps of:
immersing a first particle in a solution comprising a reducing agent and a polar solvent in order to obtain a second particle,
wherein each of the first particle and the second particle comprises a lithium manganese composite oxide with a layered rock-salt structure,
wherein the second particle comprises a first part and a second part,
wherein the second part belongs to a space group Fd-3m, and
wherein the second part is produced by immersing the first particle.
2. The method for forming an electrode material according to claim 1 , wherein the reducing agent is any one of ascorbic acid, hydrazine, dimethyl hydrazine, hydroquinone, NaBH 4 , tetra butyl ammonium bromide, LiAlH 4 , ethylene glycol, polyethylene glycol and N,N-diethylhydroxylamine.
3. The method for forming an electrode material according to claim 1 , wherein the solution further comprises water.
4. The method for forming an electrode material according to claim 1 ,
wherein the first part belongs to a space group C2/c, and
wherein the first part is larger proportion than the second part in volume.
5. The method for forming an electrode material according to claim 1 , wherein the lithium manganese composite oxide further comprises Ni.
6. The method for forming an electrode material according to claim 1 ,
wherein the lithium manganese composite oxide is represented by Li x Mn y Ni z O w , and
wherein 0≤x/(y+z)<2,y>0,z>0, and 0.26≤(y+z)/w<0.5 are satisfied.
7. A method for forming a positive electrode, comprising the steps of:
the method according to claim 1 ; and
applying slurry comprising the first particle to a current collector,
wherein applying the slurry is performed before immersing the first particle.
8. A method for manufacturing a storage battery, comprising the steps of:
the method according to claim 1 ;
forming a negative electrode; and
stacking the positive electrode and the negative electrode in an exterior body.
9. A method for forming an electrode material, comprising the steps of:
kneading a mixture comprising a flake of graphene oxide and a particle of a lithium manganese composite oxide with a layered rock-salt structure to form a first particle in which the particle of lithium manganese composite oxide is covered with the flake of graphene oxide; and
immersing the first particle in a solution comprising a reducing agent and a first solvent in order to obtain a second particle,
wherein the first solvent is a polar solvent.
10. The method for forming an electrode material according to claim 9 ,
wherein the second particle comprises a lithium manganese composite oxide with a layered rock-salt structure,
wherein the second particle comprises a first part and a second part,
wherein the second part belongs to a space group Fd-3m, and
wherein the second part is produced by immersing the first particle.
11. The method for forming an electrode material according to claim 9 , wherein the first solvent is water.
12. The method for forming an electrode material according to claim 9 ,
wherein the solution further comprises water, and
wherein the first solvent is not water.
13. The method for forming an electrode material according to claim 9 , wherein the lithium manganese composite oxide further comprises Ni.
14. A method for forming a positive electrode, comprising the steps of:
the method according to claim 9 ; and
applying the mixture to a current collector,
wherein applying the mixture is performed before immersing the first particle.
15. A method for forming an electrode material, comprising the steps of:
mixing a mixture comprising a flake of graphene oxide and a particle of a lithium manganese composite oxide with a layered rock-salt structure to form a first particle in which the particle of lithium manganese composite oxide is covered with the flake of graphene oxide;
immersing the first particle in a solution comprising a reducing agent and a first solvent; and
reducing the graphene oxide in the first particle in order to obtain a second particle,
wherein the first solvent is a polar solvent.
16. The method for forming an electrode material according to claim 15 ,
wherein the second particle comprises a lithium manganese composite oxide with a layered rock-salt structure,
wherein the second particle comprises a first part and a second part,
wherein the second part belongs to a space group Fd-3m, and
wherein the second part is produced by immersing the first particle.
17. The method for forming an electrode material according to claim 15 , wherein the first solvent is water.
18. The method for forming an electrode material according to claim 15 ,
wherein the solution further comprises water, and
wherein the first solvent is not water.
19. The method for forming an electrode material according to claim 15 , wherein the lithium manganese composite oxide further comprises Ni.
20. A method for forming a positive electrode, comprising the steps of:
the method according to claim 15 ; and
applying the mixture to a current collector,
wherein applying the mixture is performed before immersing the first particle.