Chemically-strengthened thin glass substrates with modified curvature and methods of manufacture

1. A chemically-strengthened thin glass article, which comprises:

a chemically-strengthened thin float glass substrate having a varied glass chemical structure which comprises metallic tin ions, host sodium alkali metal ions, invasive potassium alkali al ions originating from a chemical-strengthening ion-exchange, and reversing sodium alkali metal ions originating from a strength-relaxing reverse ion-exchange; wherein,

the glass substrate has opposing major surface regions each having a chemical structure within the varied glass chemical structure and comprising a concentration of larger invasive potassium alkali metal ions from ion-exchange which extend from the surface to a depth of diffusion, a concentration of metallic tin ions from the float process, and wherein in said surface regions the diffusion of invasive potassium alkali metal ions is asymmetrical, such that one major surface region of said surface regions is a treatment-disadvantaged major surface region containing a greater concentration of metallic tin ions in its chemical structure and as compared to an opposing surface region of said surface regions which is treatment-advantaged; and

wherein in at least one non-perimeter area of the thin glass substrate of the chemically-strengthened thin glass article, at least the treatment-advantaged surface region has been subject to strength relaxing reverse ion-exchange: having a net quantity of smaller sodium alkali metal ions from a reverse ion-exchange medium substituted in place of larger potassium alkali metal ions; and

wherein in a depth extending from the surface to 5 μm, the average ionic radius of the alkali metal ions located in the treatment-disadvantaged surface region is greater than the average ionic radius of the alkali ions located in the directly opposing treatment-advantaged surface region, and

wherein in a depth extending from 5 μm to the depth of diffusion, the average ionic radius of the alkali metal ions located in the treatment-advantaged surface region is greater than the average ionic radius of the alkali ions located in the directly opposing treatment-disadvantaged surface region; and

wherein in the chemically-strengthened thin glass article, the level of surface compressive stress of a non-perimeter area upon which reverse ion-exchange has been conducted is at least 100 MPa and the depth of compressive stress is at least 10 μm, and

wherein a net curvature induced by the sum of the volumes of the asymmetric chemical structure pivoting about a central tension region of the strengthened substrate is about zero and characterized as having a depth of bend less than 50 microns over a 50 mm span on a portion of a surface thereof subjected to reverse-ion exchange.

2. A chemically-strengthened thin glass article, which is produced by a process comprising the following steps:

providing a thin float glass substrate having a chemical structure which includes host alkali ions having an average ionic radius which are situated in the surface regions thereof, wherein the thin glass substrate has major surface regions that are opposed to each other, a treatment-advantaged surface region and a treatment-disadvantaged surface region, said surface regions each containing a concentration of metallic tin ions which are in a concentration greater in the treatment disadvantaged surface region than in the treatment-advantaged surface region;

applying an ion-exchange medium which includes invasive alkali ions having an average ionic radius larger than the average ionic radius of the host alkali ions to the treatment-advantaged surface of the substrate and the treatment-disadvantaged surface of the substrate; and

conducting ion-exchange to produce a chemically-strengthened glass substrate which has a greater sum of compressive stress in the treatment-advantaged surface region as compared to the sum of compressive stress in the treatment-disadvantaged surface region; and

providing a reverse ion-exchange medium which contains alkali ions having an average ionic radius that is smaller than the average tonic radius of the invasive ions contained in the ion-exchange medium; and

applying the reverse ion-exchange medium to at least one non-perimeter area of the thin glass substrate of the chemically-strengthened thin glass article on:

(1) only the treatment-advantaged surface region and conducting reverse ion-exchange to reduce the sum of compressive stress in the treatment-advantaged surface region, or

(2) the treatment-advantaged surface region and the directly opposing treatment-disadvantaged surface region and conducting reverse ion-exchange wherein the reverse ion-exchange process differs by at least one of time, temperature and exchange medium between the opposing surface regions to more greatly reduce the sum of compressive stress in the treatment-advantaged surface region than in the directly opposing treatment-disadvantaged surface region; and

wherein in the chemically-strengthened thin glass article, the level of surface compressive stress of a non-perimeter area upon which reverse ion-exchange has been conducted is at least 100 MPa and the depth of compressive stress is at least 10 μm, and

wherein, a net curvature induced by the sum of the compressive stresses in said treatment-disadvantaged surface region and said treatment-advantaged surface region pivoting about a central tension region in the strengthened substrate is about zero and characterized as having a depth of bend less than 50 microns over a 50 mm span on a portion of a surface thereof subjected to reverse-ion exchange.

3. The chemically-strengthened thin glass article of claim 2 , which is produced by a process further comprising:

measuring net curvature from that of a true flat plane in the strengthened thin glass article and then conducting a step of reverse ion-exchange to induce a curvature opposed to said measured net curvature, wherein a quantitative adjustment to the step of reverse ion-exchange is made by at least one of time, temperature and exchange medium.

4. The chemically-strengthened thin glass article of claim 1 , 2 , or 3 wherein reverse ion-exchange is conducted absent a band around the perimeter.