Method of producing glass-fiber-reinforced thermoplastic resin molded object and glass-fiber-reinforced thermoplastic resin molded object obtained by the method
Provided are a method of producing a glass-fiber-reinforced thermoplastic resin molded object by which a special glass-fiber-reinforced thermoplastic resin molded object excellent in mechanical strength and aesthetic appearance can be easily produced, and a glass-fiber-reinforced thermoplastic resin molded object obtained by the method. Glass fiber chopped strands subjected to a surface treatment with at least one of a urethane-based sizing agent and an acrylic urethane-based sizing agent, the glass fiber chopped strands each having a fiber length of from 1.2 mm to 1.8 mm, and a thermoplastic resin are each directly loaded into an injection molding machine, and are subjected to injection molding to produce the following special glass-fiber-reinforced thermoplastic resin molded object. The resin molded object shows a specific fiber length distribution and shows a specific tensile strength, and unopened glass fibers are absent on the surface of the resin molded object.
1. A method of producing a glass-fiber-reinforced polyamide-based resin molded object, comprising:
directly loading a polyamide-based resin and glass fiber chopped strands subjected to a surface treatment with at least one of a urethane-based sizing agent and an acrylic urethane-based sizing agent, the glass fiber chopped strands each having a fiber length of from 1.2 mm to 1.8 mm into an injection molding machine, and
injection molding thereof to provide a glass-fiber-reinforced polyamide-based resin molded object,
wherein the polyamide-based resin molded object has dispersed therein fibrous fillers including glass fibers,
wherein the content of all glass fibers in the glass-fiber-reinforced polyamide-based resin molded object is from 25 wt. % to 65 wt. %,
wherein the glass fibers in the glass-fiber-reinforced polyamide-based resin molded object have a fiber length described in the following (A) to (D), and are dispersed at ratios with respect to a total number of the fibrous fillers described in the following (A) to (D), and
wherein, in the glass-fiber-reinforced polyamide-based resin molded object, a property described in the following (β) is satisfied together with a physical property described in the following (α):
(A) 0.05 mm or more and less than 0.3 mm: from 30% to 60%;
(B) 0.3 mm or more and less than 0.6 mm: from 30% to 60%;
(C) 0.6 mm or more and less than 1.2 mm: from 3% to 20%;
(D) 1.2 mm or more: 0% or more and less than 1%;
(α) the glass-fiber-reinforced polyamide-based resin molded object has, when formed as an ISO multipurpose dumbbell by injection molding, a tensile strength (MPa) under an atmosphere at 25° C. of more than a value Y (MPa) represented by the following equation (1):
Y =−0.05 X 2 +6 X +70 (1)
where X represents a content (wt. %) of all the glass fibers in the glass-fiber-reinforced polyamide-based resin molded object; and
(β) unopened glass fibers are absent on a surface of a plate material, the plate material being obtained by forming the glass-fiber-reinforced polyamide-based resin molded object by injection molding as the plate material measuring 170 mm long by 50 mm wide by 12 mm thick.
2. The method of producing a glass-fiber-reinforced polyamide-based resin molded object according to claim 1 , wherein the glass fiber chopped strands each having a fiber length of from 1.2 mm to 1.8 mm comprise glass fiber chopped strands subjected to a surface treatment with the acrylic urethane-based sizing agent.
3. A glass-fiber-reinforced polyamide-based resin molded object, comprising:
a polyamide-based resin molded object having dispersed therein fibrous fillers including glass fibers subjected to a surface treatment with at least one of a urethane-based sizing agent and an acrylic urethane-based sizing agent,
wherein the content of all glass fibers in the glass-fiber-reinforced polyamide-based resin molded object is from 25 wt. % to 65 wt. %,
wherein the glass fibers have a fiber length described in the following (A) to (D), and are dispersed at ratios with respect to a total number of the fibrous fillers described in the following (A) to (D), and wherein a property described in the following (β) is satisfied together with a physical property described in the following (α):
(A) 0.05 mm or more and less than 0.3 mm: from 30% to 60%;
(B) 0.3 mm or more and less than 0.6 mm: from 30% to 60%;
(C) 0.6 mm or more and less than 1.2 mm: from 3% to 20%;
(D) 1.2 mm or more: 0% or more and less than 1%;
(α) the glass-fiber-reinforced polyamide-based resin molded object has, when formed as an ISO multipurpose dumbbell by injection molding, a tensile strength (MPa) under an atmosphere at 25° C. of more than a value Y (MPa) represented by the following equation (1):
Y =−0.05 X 2 +6 X +70 (1)
where X represents a content (wt. %) of all the glass fibers in the glass-fiber-reinforced polyamide-based resin molded object; and
(β) unopened glass fibers are absent on a surface of a plate material, the plate material being obtained by forming the glass-fiber-reinforced polyamide-based resin molded object by injection molding as the plate material measuring 170 mm long by 50 mm wide by 12 mm thick.
4. The glass-fiber-reinforced polyamide-based resin molded object according to claim 3 , wherein the glass fibers comprise glass fibers subjected to a surface treatment with the acrylic urethane-based sizing agent.