Use of dithiophosphinic acid and/or its salts for producing anti-corrosion coatings that are devoid of chrome
Use of dithiophosphinic acids of the general formula HS 2 P(R 1 )(R 2 ) and/or salts thereof for producing chrome-free, polymer-containing corrosion control layers on metallic surfaces, R 1 and R 2 independently of one another each being organic radicals having 1 to 30 C atoms.
1. A coating in combination with a metallic surface, the coating comprising a radiation-crosslinked polymer positioned on the metallic surface, wherein the crosslinked polymer comprises:
a radiation crosslinked, polymeric binder of a (meth)acrylate monomer, or (meth)acrylate prepolymer selected from the group consisting of polyfunctional (meth)acrylates, urethane (meth)acrylates, polyester (meth)acrylates, epoxy (meth)acrylates, carbonate (meth)acrylates, polyether (meth)acrylates, and any mixture thereof, and
0.25% to 10% by weight of at least one dithiophosphinic acid of formula HS 2 P(R 1 )(R 2 ) and/or a salt thereof, wherein R 1 and R 2 are, independently of one another, organic radicals with 1 to 20 carbon atoms,
wherein the coating is a chrome-free corrosion control coating, and has a thickness of from 3 to 15 μm.
2. The coating of claim 1 , wherein the polymeric binder is a copolymer of (meth)acrylic acid and one or more comonomers that include an ethylenically unsaturated group and an acidic group.
3. The coating of claim 2 , wherein the one or more comonomers is selected from vinyl acetic acid, crotonic acid, isocrotonic acid, maleic acid, fumaric acid, vinylphosphonic acid, allylphosphonic acid, 3-butenylphosphonic acid, monovinyl phosphate, monoallyl phosphate, mono-3-butenyl phosphate, phosphonoxyethyl (meth)acrylate, or styrenesulfonic acid.
4. The coating of claim 1 , wherein R 1 and R 2 , independently of one another, are selected from methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, n-nonyl, n-decyl, n-dodecyl, 2-ethylhexyl, cyclopentyl, cyclohexyl, phenyl or 4-methylphenyl.
5. The coating of claim 1 , wherein the polymeric binder further includes a polymer selected from the group consisting of poly(meth)acrylates, partially hydrolyzed polyvinyl esters, polyesters, alkyd resins, polylactones, polycarbonates, polyethers, epoxy resin-amine adducts, polyureas, polyamides, polyimides or polyurethanes.
6. The coating of claim 1 , wherein the polymeric binder further includes a polymer selected from polyesters or epoxy resin-amine adducts.
7. The coating of claim 1 , wherein the crosslinked polymer comprises a radiation crosslinked, prepolymer of urethane (meth)acrylates a number-average molar mass M n of from 500 g/mol to 10,000 g/mol, and a (meth)acrylic group content of 2 to 4 mole of (meth)acrylate units per kg of prepolymer.
8. The coating of claim 1 , wherein the at least one dithiophosphinic acid is present from 1% to 6% by weight.
9. The coating of claim 1 , wherein the at least one dithiophosphinic acid is present from 2% to 5% by weight.
10. The coating of claim 9 , wherein the at least one dithiophosphinic acid is selected from di-p-tolyldithiophosphinic acid, diisobutylthiophosphinic acid, dicyclohexylthiophosphinic acid, or the corresponding acid salts thereof.
11. The coating of claim 1 , applied as a coil coating to a surface treated steel coil.
12. An aqueous integrated coating in combination with a metallic surface, the coating comprising a styrene-acrylate dispersion, an anticorrosion pigment based on zinc phosphate, and 0.25% to 10% by weight of at least one dithiophosphinic acid of formula HS 2 P(R 1 )(R 2 ) and/or a salt thereof, wherein R 1 and R 2 are, independently of one another, organic radicals with 1 to 20 carbon atoms,
wherein the integrated coating, and has a thickness of from 40 to 100 μm.
13. The integrated, coating of claim 12 , wherein the at least one dithiophosphinic acid is present from 0.25% to 5% by weight.
14. The integrated coating of claim 12 , wherein the at least one dithiophosphinic acid is an ammonium acid salt.