Methods of making electroactive composite materials for an electrochemical cell
Methods for making electroactive composite materials for electrochemical cells are provided. The method includes introducing a particle mixture comprising a first particle having a first diameter (R 1 ) and comprising a first electroactive material and a second particle having a second diameter (R 2 ) smaller than the first diameter (R 1 ) and comprising a second electroactive material into a dry-coating device having a rotatable vessel defining a cavity and a rotor disposed therewithin. The vessel is rotated at a first speed in a first direction, and the rotor is rotated at a second speed greater than the first speed in a second direction opposing the first direction. The particle mixture flows between cavity walls and the rotor and experiences thrusting and compression forces that create a substantially uniform coating comprising the second electroactive material on one or more exposed surfaces of the first particle.
1. A method of making an electroactive composite material for an electrochemical cell, the method comprising:
introducing a particle mixture into a dry-coating device comprising a rotatable vessel having a wall defining a cavity and a rotor disposed within the cavity, wherein the particle mixture includes a first particle having a first average diameter (R 1 ) that comprises a first electroactive material comprising graphite and a second particle having a second average diameter (R 2 ) that comprises a second electroactive material comprising silicon (Si), wherein the first average diameter (R 1 ) is greater than the second average diameter (R 2 );
rotating the rotatable vessel at a first speed in a first direction; and
rotating the rotor at a second speed greater than the first speed in a second direction opposite to the first direction, wherein a minimum clearance (C) between the wall of the cavity and the rotor is greater than or equal to a sum of the first average diameter (R 1 ) and two times the second average diameter (R 2 ), so that C≥R 1 +2R 2 ,
wherein the particle mixture flows between the wall defining the cavity and the rotor at the clearance to create a substantially uniform coating comprising the second electroactive material on one or more exposed surfaces of the first particle.
2. The method of claim 1 , wherein the substantially uniform coating comprising the second electroactive material covers greater than or equal to about 70% of the exposed surface of the first particle.
3. The method of claim 1 , wherein the particle mixture includes less than or equal to about 95 weight % of the first particle and greater than or equal to about 5 weight % of the second particle.
4. The method of claim 1 , wherein the first average diameter (R 1 ) of the first particle is greater than or equal to about 1 μm to less than or equal to about 100 μm, and the second average diameter (R 2 ) of the second particle is less than or equal to about 5 μm.
5. The method of claim 1 , wherein the minimum clearance (C) is greater than or equal to about 0.05 mm and less than or equal to about 1 mm.
6. The method of claim 1 , wherein the cavity and rotor of the dry-coating device each have an elliptical cross sectional shape.
7. The method of claim 1 , wherein the vessel and rotor are rotated for a time greater than or equal to about 5 minutes to less than or equal to 120 minutes.
8. The method of claim 1 , wherein the first speed is greater than or equal to about 50 rpm to less than or equal to about 100 rpm, and the second speed is greater than or equal to about 1000 rpm to less than or equal to about 6000 rpm.
9. A solvent-free method of making an electroactive composite material for an electrochemical cell, the method comprising:
introducing a particle mixture into a dry-coating device comprising a rotatable vessel having a wall defining a cavity with an elliptical cross-sectional shape and an elliptical shaped rotor disposed within the cavity, wherein the particle mixture comprises a first particle comprising a first electroactive material that comprises graphite and a second particle comprising a second electroactive material that comprises silicon (Si), wherein the first particle has a first average diameter (R 1 ) that is greater than or equal to about 1 μm to less than or equal to about 100 μm and the second particle has a second average diameter (R 2 ) that is less than or equal to about 5 μm;
rotating the rotatable vessel at a first speed in a first direction; and
rotating the elliptical shaped rotor at a second speed greater than the first speed in a second direction opposing the first direction, wherein a minimum clearance (C) between the wall of the cavity and the rotor is greater than or equal to a sum of the first average diameter (R 1 ) and two times the second average diameter (R 2 ), so that C≥R 1 +2R 2 ;
wherein the particle mixture flows between the wall defining the cavity and the elliptical shaped rotor at the clearance that creates a substantially uniform coating comprising the second electroactive material on one or more exposed surfaces of the first particle.
10. The method of claim 9 , wherein the minimum clearance (C) is greater than or equal to about 0.05 mm and less than or equal to about 1 mm.
11. The method of claim 9 , wherein the substantially uniform coating comprising the second electroactive material covers greater than or equal to about 70% of the exposed surface of the first particle and has a thickness of greater than or equal to about 1 nm to less than or equal to about 1 μm.
12. The method of claim 9 , wherein the particle mixture includes less than or equal to about 95 weight % of the first particle and greater than or equal to about 5 weight % of the second particle.
13. The method of claim 9 , wherein the vessel and rotor are rotated for a time greater than or equal to 5 minutes to less than or equal to 120 minutes, the first speed is greater than or equal to about 50 rpm to less than or equal to about 100 rpm, and the second speed is greater than or equal to about 1000 rpm to less than or equal to about 6000 rpm.
14. A method of making an electroactive composite material for an electrochemical cell, the method comprising:
introducing a particle mixture into a dry-coating device comprising a rotatable vessel having a wall defining a cavity and a rotor disposed within the cavity, wherein the particle mixture includes a first particle having a first average diameter (R 1 ) that includes a first electroactive material comprising a positive electrode material selected from the group consisting of silicon (Si), lithium manganese nickel cobalt oxide (LiNiMnCoO 2 ), and combinations thereof and a second particle having a second average diameter (R 2 ) that includes a second electroactive material selected from the group consisting of graphite, graphene, graphene platelet, and combinations thereof, wherein the first average diameter (R 1 ) is greater than the second average diameter (R 2 );
rotating the rotatable vessel at a first speed in a first direction; and
rotating the rotor at a second speed greater than the first speed in a second direction opposite to the first direction, wherein a minimum clearance (C) between the wall of the cavity and the rotor is greater than or equal to a sum of the first average diameter (R 1 ) and two times the second average diameter (R 2 ), so that C≥R 1 +2R 2 ,
wherein the particle mixture flows between the wall defining the cavity and the rotor at the clearance so that the rotor exfoliates the second electroactive material to create a substantially uniform coating comprising the second electroactive material on one or more exposed surfaces of the first particle.
15. The method of claim 14 , wherein the substantially uniform coating comprising the second electroactive material covers greater than or equal to about 70% of the exposed surface of the first particle.
16. The method of claim 14 , wherein the particle mixture includes less than or equal to about 95 weight % of the first particle and greater than or equal to about 5 weight % of the second particle.
17. The method of claim 14 , wherein the first average diameter (R 1 ) of the first particle is greater than or equal to about 1 μm to less than or equal to about 100 μm, and the second average diameter (R 2 ) of the second particle is less than or equal to about 5 μm.
18. The method of claim 14 , wherein the clearance is greater than or equal to about 0.05 mm and less than or equal to about 1 mm.
19. The method of claim 14 , wherein the cavity and rotor of the dry-coating device each have an elliptical cross sectional shape.
20. The method of claim 14 , wherein the vessel and rotor are rotated for a time greater than or equal to about 5 minutes to less than or equal to 120 minutes; and wherein the first speed is greater than or equal to about 50 rpm to less than or equal to about 100 rpm, and the second speed is greater than or equal to about 1000 rpm to less than or equal to about 6000 rpm.