Dental materials using thermoset polymers
Provided herein are crosslinked polymers useful in orthodontic appliances and light polymerizable liquid compositions and formulations useful for making crosslinked polymers. Also provided are methods of making an orthodontic appliance comprising a cross-linked polymer formed by a direct fabrication technique.
1. A crosslinked polymer for use in an orthodontic appliance, the crosslinked polymer comprising:
a first repeating unit derived from a urethane (meth)acrylate oligomer;
a second repeating unit derived from a vinyl or thiol monomer; and
a tensile modulus from 800 MPa to 2000 MPa, a tensile strength at yield of 20 MPa to 55 MPa, an elongation at yield greater than 4% and an elongation at break greater than 30%.
2. The crosslinked polymer of claim 1 , wherein at least one of the urethane (meth)acrylate oligomer, the vinyl monomer and the thiol monomer comprises at least two polymerizable groups.
3. The crosslinked polymer of claim 2 , wherein the amount of the first repeating unit is from 25 to 50 wt % and the amount of the second repeating unit is from 50 to 75 wt %, with the total amount of the first repeating unit and the second repeating unit being greater than or equal to 70 wt %.
4. The crosslinked polymer of claim 1 , wherein the crosslinked polymer further comprises a third repeating unit derived from a second urethane (meth)acrylate oligomer or a second vinyl or thiol monomer not including a urethane linkage, wherein at least one of the urethane (meth)acrylate oligomer(s) and the vinyl or thiol monomer(s) comprises at least two polymerizable groups.
5. The crosslinked polymer of claim 4 , wherein the amount of the first repeating unit is from 15 to 40 wt %, the amount of the second repeating unit is from 15 to 75 wt % and the amount of the third repeating unit is from 2 to 60 wt %, with the total amount of the first repeating unit, the second repeating unit and the third repeating unit being greater than or equal to 70 wt %.
6. The crosslinked polymer of claim 4 , wherein the second repeating unit is derived from a vinyl monomer not including a urethane linkage.
7. The crosslinked polymer of claim 4 , wherein the second repeating unit is derived from 1-vinyl-2-pyrrolidinone (NVP), β-carboxyethylacrylate-(CEA), trimethyl cyclohexyl acrylate (TMCHA), tetrahydrofurfuryl methacrylate (THFMA), isobornyl acrylate (IBOA), or isobornyl methacrylate (IBOMA).
8. The crosslinked polymer of claim 1 , wherein the urethane (meth)acrylate oligomer is selected from the group consisting of a urethane dimethacrylate oligomer, an isophorone urethane dimethacrylate oligomer, a urethane diacrylate oligomer, and a urethane triacrylate oligomer.
9. The crosslinked polymer of claim 1 , wherein the second repeating unit is derived from an acrylate monomer.
10. The crosslinked polymer of claim 1 , wherein the crosslinked polymer has a transmittance equal to or greater than 80% for light having a wavelength in the visible region.
11. The crosslinked polymer of claim 1 , wherein the crosslinked polymer comprises a plurality of polymer layers.
12. The crosslinked polymer of claim 1 , wherein the crosslinked polymer is transparent, translucent, or opaque.
13. The crosslinked polymer of claim 4 , wherein the third repeating unit is derived from a urethane (meth)acrylate oligomer or vinyl monomer not including a urethane linkage.
14. The crosslinked polymer of claim 4 , wherein the third repeating unit is derived from a thiol monomer.