Method to improve surface finish of glass fiber mat

1. A method for making a gypsum product, the method comprising:

obtaining a glass fiber mat;

laminating the glass fiber mat with a thermosetting polymeric resin by soaking the glass fiber mat in the thermosetting polymeric resin;

partially curing the thermosetting polymeric resin;

after the thermosetting polymeric resin is partially cured, but before the thermosetting polymeric resin is fully cured, compressing glass fibers in the glass fiber mat by at least one of the following means: in a wet press under a pressure in the range from 5 psi to 100 psi, and/or by a calendar;

curing the thermosetting polymeric resin by exposing it to heat;

preparing a gypsum slurry;

depositing the gypsum slurry onto the cured laminated glass fiber mat; and

letting the gypsum product set.

2. The method of claim 1 , where the cured laminated glass fiber mat has a face side and a back side, and the back side is in contact with the gypsum slurry.

3. The method of claim 1 , wherein glass fibers in the glass fiber mat are compressed to produce a level 5 finish for the gypsum product.

4. The method claim 2 , wherein the fibers on the face side are compressed.

5. The method of claim 1 , wherein the thermosetting polymeric resin is an acrylic binder.

6. The method of claim 1 , wherein the gypsum slurry further comprises at least one of the following: foam, natural fibers, synthetic fibers, a defoamer, a plastisizer, a filler and a binder.

7. A method for making a laminated glass fiber mat, the method comprising:

obtaining a glass fiber mat;

soaking it in a thermosetting polymeric resin;

partially curing the thermosetting polymeric resin;

after the thermosetting polymeric resin is partially cured, but before the thermosetting polymeric resin is fully cured, compressing the fibers in the glass fiber mat with a wet press under the pressure in the range from 5 psi to 100 psi and/or by a calendar; and

curing the laminated glass fiber mat in a dryer.

8. The method of claim 7 , wherein the glass fiber mat is further pressed with a dry press before it is soaked.

9. The method of claim 7 , wherein the glass fiber mat is further calendared after the resin is cured.

10. The method of claim 7 , wherein the glass fiber mat is further calendared before the resin is fully cured.

11. The method of claim 7 , wherein a calendar is used in place of a wet press and the resin is only partially cured with a first dryer before the calendaring step.

12. The method of claim 11 , wherein the resin is cured to completion with a second dryer after the calendaring step.

13. The method of claim 1 , wherein the thermosetting polymeric resin is selected from a polyacrylate, polystyrene, polyester, polyethylene, polypropylene, polybutylene and mixtures thereof.

14. The method of claim 1 , wherein the step of compressing comprises applying a pressure of up to 60 psi.