Method of making coextruded, crosslinked multilayer polyolefin foam structures from recycled crosslinked polyolefin foam material
The present disclosure is directed to a physically crosslinked, closed cell continuous multilayer foam structure comprising at least one foam polypropylene/polyethylene layer with a recycled polyolefin material layer. The multilayer foam structure can be obtained by coextruding a multilayer structure comprising at least one nonrecycled foam composition layer with at least one recycled foam composition layer, irradiating the coextruded structure with ionizing radiation, and continuously foaming the irradiated structure.
1. A method of forming a multilayer structure comprising:
shredding a polyolefin foam, agglomerating the shredded foam, and granulating the agglomerated foam to form a recycled, crosslinked polyolefin foam material; and
coextruding:
a first layer comprising:
polypropylene, polyethylene, or a combination of polypropylene and polyethylene; and
a first chemical foaming agent; and
a second layer on a side of the first layer, the second layer comprising:
2.5-25 wt. % the recycled, crosslinked polyolefin foam material;
75-97.5 wt. % polypropylene, polyethylene, or a combination of polypropylene and polyethylene; and
a second chemical foaming agent.
2. The method of claim 1 , wherein the granules of the recycled, crosslinked polyolefin foam material have a width of 3-7 mm.
3. The method of claim 1 , further comprising mechanically pulverizing the granules of the recycled, crosslinked polyolefin foam material.
4. The method of claim 3 , wherein particles of the mechanically pulverized recycled, crosslinked polyolefin foam material have a width of 0.2-2 mm.
5. The method of claim 1 , further comprising coextruding a third layer on a side of the second layer opposite the first layer, the third layer comprising:
polypropylene or polyethylene; and
a third chemical foaming agent.
6. The method of claim 5 , wherein the first layer and the third layer are substantially free of recycled polyolefin material.
7. The method of claim 5 , wherein the first, second, and third layers comprise a crosslinking agent.
8. The method of claim 5 , wherein the first, second, and third chemical foaming agent is azodicarbonamide.
9. The method of claim 5 , wherein the first layer and third layer comprise polypropylene and polyethylene.
10. The method of claim 1 , wherein the first layer comprises polypropylene with a melt flow index of 0.1-25 grams per 10 minutes at 230° C.
11. The method of claim 1 , wherein the first layer comprises polyethylene with a melt flow index of 0.1-25 grams per 10 minutes at 190° C.
12. A method of forming a multilayer foam structure comprising:
shredding a polyolefin foam, agglomerating the shredded foam, and granulating the agglomerated foam to form a recycled, crosslinked polyolefin foam material;
coextruding:
a first layer comprising:
polypropylene or polyethylene; and
a first chemical foaming agent; and
a second layer on a side of the first layer, the second layer comprising:
2.5-25 wt. % the recycled, crosslinked polyolefin foam material;
75-97.5 wt. % polypropylene, polyethylene, or a combination of polypropylene and polyethylene; and
a second chemical foaming agent;
irradiating the coextruded layers with ionizing radiation; and
foaming the irradiated, coextruded layers.
13. The method of claim 12 , further comprising coextruding a third layer on a side of the second layer opposite the first layer, the third layer comprising:
polypropylene or polyethylene; and
a third chemical foaming agent.
14. The method of claim 13 , wherein the first layer and the third layer are substantially free of recycled polyolefin material.
15. The method of claim 13 , wherein the first layer and third layer comprise polypropylene and polyethylene.
16. The method of claim 12 , wherein the granules of the recycled, crosslinked polyolefin foam material have a width of 3-7 mm.
17. The method of claim 12 , further comprising mechanically pulverizing the granules of the recycled, crosslinked polyolefin foam material.
18. The method of claim 17 , wherein particles of the mechanically pulverized recycled, crosslinked polyolefin foam material have a width of 0.2-2 mm.
19. The method of claim 12 , wherein the ionizing radiation is selected from the group consisting of alpha, beta (electron), x-ray, gamma, and neutron.
20. The method of claim 12 , wherein the coextruded structure is irradiated up to 4 separate times.
21. The method of claim 20 , wherein the ionizing radiation is an electron beam with an acceleration voltage of 200-1500 kV.
22. The method of claim 21 , wherein an absorbed electron beam dosage is 10-500 kGy.
23. The method of claim 12 , wherein the ionizing radiation crosslinks the extruded structure to a crosslinking degree of 20-75%.
24. The method of claim 12 , wherein foaming comprises heating the irradiated structure with molten salt.
25. The method of claim 12 , wherein the multilayer foam structure has a density of 20-250 kg/m 3 .
26. The method of claim 12 , wherein the multilayer foam structure has an average closed cell size of 0.05-1.0 mm.
27. The method of claim 12 , wherein the multilayer foam structure has a thickness of 0.2-50 mm.
28. The method of claim 12 , wherein a mean surface roughness for the first layer is less than 80 μm.