Bimodal polypropylene and process for the preparation thereof
The present invention relates to a polypropylene composition comprising: a first polypropylene homopolymer or random copolymer (PPR1) having a comonomer content lower than the comonomer content of the second polypropylene, a second polypropylene (PPR2) which is a random copolymer of propylene and of the comonomer; said comonomer being an alpha-olefin different from propylene, the melting temperature of the polypropylene composition (T m (PPR)) being defined as T m (PPR)>165−6.9*[total comonomer content]−8.4*[comonomer content of the first polypropylene], the difference between the melting temperature and the crystallization temperature of the polypropylene composition ranges from 27 and 33, and a xylene soluble fraction (XS) at 23° C. of not more than 1.5 wt. %. The present invention also relates to a process for the preparation of said polypropylene composition. The present invention further relates to the use of said polypropylene composition for producing films or moulded articles.
1. A polypropylene composition (PPR) comprising:
(A) a first polypropylene homopolymer or random copolymer (PPR1) having a comonomer content from 0 to lower than the comonomer content of the second polypropylene,
(B) a second polypropylene (PPR2) which is a random copolymer of propylene and of the comonomer;
wherein:
the polypropylene composition has a total comonomer content ranging from 0.25 to 4.5 wt % based on the total weight of the polypropylene composition,
the comonomer is selected from the group consisting of ethylene, butene-1, pentene-1, hexene-1 and 4-methyl-1-pentene,
the melting temperature, measured by DSC based on ISO 3146, of the polypropylene composition (T m (PPR)) is defined as
T m (PPR)>165−6.9×[total comonomer content]−8.4×[comonomer content of the first polypropylene],
the difference between the melting temperature and the crystallization temperature, both measured by DSC, of the polypropylene composition ranges from 27 to 33,
a xylene soluble fraction (XS) of not more than 1.5 wt %, and wherein the polypropylene composition has a melt flow index ranging from 20 to 200 g/10 min, the values of melt flow index being measured according to ISO 1133 at (230° C., under a 2.16 kg load), and
a regiodefects content ranging from 0.1% to 5%.
2. A polypropylene composition according to claim 1 wherein the comonomer is ethylene.
3. A polypropylene composition according to claim 1 wherein the melt flow index of the first polypropylene is greater than the melt flow index of the second polypropylene; the values of melt flow index being measured according to ISO 1133 (230° C., 2.16 kg load).
4. A polypropylene composition according to claim 1 wherein the melt flow index of the first polypropylene has a melt flow index ranging from 1 to 200 g/10 min and the second polypropylene has a melt flow index ranging from 1 to 200 g/10 min.
5. A polypropylene composition according to claim 1 having a flexural modulus greater than 1000 MPa, the flexural modulus being measured at 23° C. according to ISO 178.
6. A polypropylene composition according to claim 1 having notched Izod impact strength between 3.0 and 4.0 kJ/m 2 .
7. A process for the preparation of the polypropylene composition comprising the steps of:
(i) providing a first polypropylene having a comonomer content from 0 to lower than the comonomer content of the second polypropylene,
(ii) providing a second polypropylene which is a random copolymer of propylene and of the comonomer,
(iii) recovering the polypropylene composition having a total comonomer content ranging from 0.25 and 4.5 wt % based on the total weight of the polypropylene composition,
wherein steps (i) and (ii) are carried out by polymerizing propylene and, if any, the comonomer in presence of a metallocene-based polymerization catalyst, wherein the polypropylene composition comprises:
(A) a first polypropylene homopolymer or random copolymer (PPR1) having a comonomer content from 0 to lower than the comonomer content of the second polypropylene,
(B) a second polypropylene (PPR2) which is a random copolymer of propylene and of the comonomer;
wherein:
the polypropylene composition has a total comonomer content ranging from 0.25 to 4.5 wt % based on the total weight of the polypropylene composition,
the comonomer is selected from the group consisting of ethylene, butene-1, pentene-1, hexene-1 and 4-methyl-1-pentene,
the melting temperature, measured by DSC based on ISO 3146, of the polypropylene composition (T m (PPR)) is defined as
T m (PPR)>165−6.9×[total comonomer content]−8.4×[comonomer content of the first polypropylene],
the difference between the melting temperature and the crystallization temperature, both measured by DSC, of the polypropylene composition ranges from 27 to 33,
a xylene soluble fraction (XS) of not more than 1.5 wt. %, and wherein the polypropylene composition has a melt flow index ranging from 20 to 200 g/10 min, the values of melt flow index being measured according to ISO 1133 at (230° C., under a 2.16 kg load), and
a regiodefects content ranging from 0.1% to 5%.
8. A process according to claim 7 wherein the comonomer content of the first polypropylene is lower than 3.5 wt % based on the total weight of the first polypropylene.
9. A process according to claim 8 , wherein the comonomer content of the second polypropylene is greater than 1.5 wt % and is at most 8.0 wt %, preferably ranges from 1.5 to 6.0 wt % based on the total weight of the second polypropylene.
10. A process according to claim 8 wherein step (iii) is carried out by blending the first polypropylene and the second polypropylene or by mixing the first polypropylene to the second polypropylene simultaneously to the preparation thereof.
11. An article comprising a polypropylene composition according to claim 1 .
12. A method comprising using the polypropylene composition according to claim 1 for the production of films or moulded articles.