Methods of removing a ceramic coating from a substrate
A method for removing a ceramic coating from a substrate is presented. The method includes contacting the ceramic coating with a composition including a fluoride source and nitric acid. A method of forming a component having a variation in saturation magnetization is presented. The method includes masking selected portions of a surface of a metallic component using a ceramic coating to form a masked metallic component; selectively diffusing nitrogen into the metallic component by exposing the masked metallic component to a nitrogen-rich atmosphere; and removing the ceramic coating from the surface of the metallic component by contacting the ceramic coating with a composition including the fluoride source and nitric acid.
1. A method for removing a ceramic coating from a substrate, comprising:
applying the ceramic coating as a patterned mask over the substrate to define a masked portion and an unmasked portion thereon, wherein the ceramic coating comprises aluminum silicide, sodium aluminum silicate, potassium aluminum silicate, sodium potassium aluminum silicate, or combinations thereof, and wherein the substrate is a magnetic component; and
contacting the ceramic coating with a composition comprising a fluoride source and nitric acid.
2. The method of claim 1 , wherein the fluoride source comprises hydrofluoric acid.
3. The method of claim 1 , wherein the fluoride source comprises ammonium fluoride, ammonium bifluoride, sodium fluoride, potassium fluoride, lithium fluoride, or combinations thereof.
4. The method of claim 1 , wherein an amount of the fluoride source in the composition is in a range from about 5 weight % to about 30 weight %.
5. The method of claim 1 , wherein an amount of the nitric acid in the composition is in a range from about 50 weight % to about 95 weight %.
6. The method of claim 1 , wherein the ceramic coating is contacted with the composition at a temperature in a range from about 25° C. to about 60° C.
7. The method of claim 1 , wherein the ceramic coating is contacted with the composition for a time duration in a range from about 10 min to about 60 min.
8. The method of claim 1 , wherein the substrate comprises a metal alloy.
9. The method of claim 1 , wherein the ceramic coating comprises the sodium-potassium-aluminum-silicate.
10. The method of claim 1 , wherein the ceramic coating includes at least one alkali metal.
11. The method of claim 10 , wherein the at least one alkali metal comprises sodium.
12. The method of claim 10 , wherein the at least one alkali metal comprises potassium.
13. A method for removing a ceramic coating from a substrate, comprising:
applying the ceramic coating as a patterned mask over the substrate to define a masked portion and an unmasked portion thereon, wherein the ceramic coating comprises aluminum silicide, sodium aluminum silicate, potassium aluminum silicate, sodium potassium aluminum silicate, or combinations thereof, and wherein the substrate comprises an iron-based alloy; and
contacting the ceramic coating with a composition comprising a fluoride source and nitric acid.
14. The method of claim 13 , wherein the iron-based alloy includes 14 weight % and 20 weight % chromium and between 2 weight % and 5 weight % of manganese with the balance being iron.
15. A method for removing a ceramic coating from a substrate, comprising:
applying the ceramic coating as a patterned mask over the substrate to define a masked portion and an unmasked portion thereon, wherein the ceramic coating comprises aluminum silicide, sodium aluminum silicate, potassium aluminum silicate, sodium potassium aluminum silicate, or combinations thereof,
exposing the substrate to a nitrogen-rich atmosphere such that nitrogen selectively diffuses into the unmasked portion; and
thereafter, contacting the ceramic coating with a composition comprising a fluoride source and nitric acid.