Honeycomb structure and method for manufacturing the same

1. A honeycomb structure comprising:

promoter particles which contain at least first promoter particles made of a ceria-zirconia solid solution; and

a binder phase in which a number of inorganic binder particles are aggregated with each other, with α-alumina being a main component, the inorganic binder particles interposed between the promoter particles, wherein

the honeycomb structure is obtained by sintering at a temperature of 1100° C. or less

the binder phase contain Fe and/or Cr dissolved in α-alumina; and

the honeycomb structure has a specific surface area at a ratio of 90% or more after heating to before heating at 1200° C. for 20 hours.

2. The honeycomb structure as set forth in claim 1 , wherein,

the promoter particles contain second promoter particles made of one or two of γ-alumina and θ-alumina.

3. A manufacturing method of the honeycomb structure as set forth in claim 1 comprising:

a mixing step of obtaining a clay by mixing at least the promoter particles, an inorganic binder material made of alumina sol, and a sintering assistant solution that is an aqueous solution of one or two of an Fe salt and a Cr salt, the promoter particles containing at least the first promoter particles made of a ceria-zirconia solid solution; and

a molding step of obtaining a molding by molding the clay into a honeycomb shape;

a sintering step of sintering the molding at a temperature of 1100° C. or less, wherein

in the mixing step, the sintering assistant solution is added so that an addition amount of one or two of Fe and Cr are 1.4 parts by mass or less in terms of an amount of oxide, relative to 100 parts by mass of the promoter particles.

4. The manufacturing method of the honeycomb structure as set forth in claim 3 , wherein,

in the mixing step, a liquid mixture is prepared by mixing the inorganic binder material and the sintering assistant solution in advance; and

the promoter particles are added to the liquid mixture.