Metal powders and use thereof
A new pre-alloyed metal based powder, intended to be used in surface coating of metal parts. The powder is deposited using e.g. laser cladding or plasma transfer arc welding (PTA), or thermal spray (e.g. HVOF). The powder is useful for reducing friction and improving wear reducing properties of the deposited coating. Such coatings may also improve machinability. As friction or wear reducing component, inclusions of manganese sulphide or tungsten sulphide in the pre-alloyed powder may be used.
1. Water or gas atomized metal powder comprising, by weight:
C, 1-1.3%;
Cr, 22-27%;
Mn, 4-5%;
Ni, 3-5%;
Si, 3-4%;
Mo, 1.5-2.5%;
inclusions of MnS 4-15%;
the balance comprising Fe,
said powder being suitable for thermal surfacing.
2. The water or gas atomized metal powder of claim 1 , wherein the power consists of, by weight:
C, 1-1.3%;
Cr, 22-27%;
Mn, 4-5%;
Ni, 3-5%;
Si, 3-4%;
Mo, 1.5-2.5%;
inclusions of MnS 4-15%;
the balance consisting of Fe.
3. The water or gas atomized metal powder of claim 1 , wherein the power comprises, by weight:
C, 1.2%;
Cr, 25%;
Mn, 4.5%;
Ni, 4%;
Si, 3.3%;
Mo, 2%;
inclusions of MnS 4-15%;
the balance comprising Fe.
4. The water or gas atomized metal powder of claim 1 , wherein the power consists of, by weight:
C, 1.2%;
Cr, 25%;
Mn, 4.5%;
Ni, 4%;
Si, 3.3%;
Mo, 2%;
inclusions of MnS 4-15%;
the balance being Fe.
5. The water or gas atomized metal powder of claim 1 , wherein the amount of MnS is 4-8% by weight.
6. The water or gas atomized metal powder of claim 1 , wherein the amount of MnS is 5-7% by weight.
7. The water or gas atomized metal powder of claim 1 , wherein the particle size of the metal powder is from 45 μm to 200 μm.
8. The water or gas atomized metal powder of claim 1 , wherein the particle size of the metal powder is from 50-150 μm.
9. Method for surface coating metal parts, by way of laser cladding or PTA (plasma transferred arc), with a metal powder according to claim 1 , thereby producing a metal coated component.
10. Metal coated component produced by the method according to claim 9 .
11. Metal coated component according to claim 10 , wherein the component is selected from the group consisting of industrial valves, sheet metal forming (SMF) tools, transport rollers in iron works, paper knives, and glass moulds.