Method of producing uniform polymer beads by vibration jetting with superhydrophobic membrane
Spheroidal polymer beads having a uniform size are prepared by polymerizing uniformly sized monomer droplets formed by dispersing a polymerizable monomer phase over double-walled cylindrical cross-flow membrane into an suspension phase. A shear force is provided at a point of egression of the polymerizable monomer phase into the suspension phase, the direction of shear substantially perpendicular to the direction of egression of the monomer phase. The membrane is metallic and includes a superhydrophobic coating.
1. A method for preparing spheroidal polymer beads having a volume average particle diameter of about 10 to about 180 um, the method comprising the steps of:
providing an apparatus comprising a metallic membrane containing a plurality of through holes, wherein the metallic membrane is nickel and is coated with a superhydrophobic polytetrafluoroethylene coating, wherein a first volume is in contact with a first side of the membrane and a second volume is in contact with a second side of the membrane, the first volume comprising a polymerizable monomer phase, the second volume comprising a liquid immiscible with the monomer phase;
dispersing the first volume through the through holes into the second volume under conditions sufficient to form a plurality of monomer droplets comprising the polymerizable monomer, wherein a shear force is provided at a point of egression of the first volume into the second volume, the direction of shear substantially perpendicular to the direction of egression of the first volume, and the shear force is provided by displacing the membrane relative to the second volume; and
polymerizing the droplets dispersed in the second volume.
2. The method according to claim 1 , wherein the membrane comprises from about 200 to about 2,000 through holes per cm 2 of the membrane.
3. The method according to claim 1 , wherein the through holes have a diameter in the range of about 1 μm to about 100 μm.
4. The method according to claim 3 , wherein the through holes have a diameter in the range of about 20 μm to about 60 μm.
5. The method according to claim 1 , wherein the plurality of through holes are positioned from each other at a distance of at least about 20 times the diameter of each through hole when the distance is measured from the center of each through hole.
6. The method according to claim 1 , wherein the monomer phase is dispersed through the through holes into the second volume at a rate of about 1 to about 50 cm/s.
7. The method according to claim 1 , wherein the beads have a particle size distribution having a uniformity coefficient of less than 1.2.
8. The method according to claim 1 , wherein the displacing is rotating, pulsing, or oscillating movement.
9. The method according to claim 1 , wherein the first volume is dispersed into the second volume by applying pressure to the first volume.
10. The method according to claim 1 , wherein the membrane is nickel-plated.
11. The method according to claim 1 , wherein the plurality of through holes are conical shaped.
12. The method according to claim 1 , wherein the through holes are in the shape of a slot, with an aspect ratio of slot width to slot length of at least 1:2.
13. The method according to claim 1 , wherein the dispersed phase comprises agarose or other gel forming compounds.
14. The method according to claim 1 , wherein the polymerizable monomer phase comprises a porogen.
15. The method of claim 1 wherein the polytetrafluoroethylene coating comprises particles of polytetrafluoroethylene.
16. The method of claim 15 , wherein said particles are nanoparticles.
17. The method of claim 1 wherein the polytetrafluoroethylene coating further comprises nanoparticles of elemental nickel.
18. The method of claim 1 , wherein the superhydrophobic coating is applied to said membrane by electroless deposition.
19. The method of claim 1 , further comprising a coating of amorphous polytetrafluoroethylene applied to the upper surface of the polytetrafluoroethylene coating.
20. A method for preparing spheroidal agarose beads having a volume average particle diameter of about 10 to about 180 um, the method comprising the steps of:
providing an apparatus comprising a metallic membrane containing a plurality of through holes, wherein the metallic membrane is nickel and is coated with a superhydrophobic polytetrafluoroethylene coating, wherein a first volume is in contact with a first side of the membrane and a second volume is in contact with a second side of the membrane, the first volume comprising agarose solution, the second volume comprising a liquid immiscible with the agarose solution;
dispersing the agarose solution through the through holes into the liquid immiscible with the agarose solution under conditions sufficient to form a plurality of agarose droplets, wherein a shear force is provided at a point of egression of the first volume into the second volume, the direction of shear substantially perpendicular to the direction of egression of the first volume, and the shear force is provided by displacing the membrane relative to the second volume; and
hardening the agarose droplets dispersed in the second volume to form agarose beads.
21. The method of claim 20 wherein the polytetrafluoroethylene coating comprises particles of polytetrafluoroethylene.
22. The method of claim 21 , wherein said particles are nanoparticles.
23. The method of claim 20 , wherein the superhydrophobic coating further comprises nanoparticles of elemental nickel.
24. The method of claim 20 , wherein the superhydrophobic coating is applied to said membrane by electroless deposition.
25. The method of claim 20 further comprising a coating of amorphous polytetrafluoroethylene applied to the upper surface of the polytetrafluoroethylene coating.
26. A method for preparing spheroidal agarose beads having a volume average particle diameter of about 10 to about 180 um, the method comprising the steps of:
providing an apparatus comprising a metallic membrane containing a plurality of through holes, wherein the metallic membrane is nickel and is coated with a superhydrophobic polytetrafluoroethylene coating, wherein an aqueous agarose solution is in contact with a first side of the membrane and mineral oil is in contact with a second side of the membrane;
dispersing the agarose solution through the through holes into the mineral oil under conditions sufficient to form a plurality of agarose droplets, wherein a shear force is provided at a point of egression of the agarose solution into the mineral oil, the direction of shear substantially perpendicular to the direction of egression of the agarose solution, and the shear force is provided by displacing the membrane relative to the mineral oil; and
hardening the agarose droplets dispersed in the mineral oil to form agarose beads.
27. The method of claim 26 wherein the polytetrafluoroethylene coating comprises particles of polytetrafluoroethylene.
28. The method of claim 27 , wherein said particles are nanoparticles.
29. The method of claim 26 , wherein the superhydrophobic coating further comprises nanoparticles of elemental nickel.
30. The method of claim 26 , wherein the superhydrophobic coating is applied to said membrane by electroless deposition.
31. The method of claim 26 , wherein the agarose solution is heated before it is dispersed through the through holes.
32. The method of claim 26 further comprising a coating of amorphous polytetrafluoroethylene applied to the upper surface of the polytetrafluoroethylene coating.