Thermally expandable sheet and thermally expandable sheet production method
A thermally expandable sheet includes: a first thermally expansive layer that is formed on one side of a base and contains a first thermally expandable material and a first binder, the first thermally expansive layer having a first ratio of the first thermally expandable material with respect to the first binder; and a second thermally expansive layer that is formed on the first thermally expansive layer and contains a second thermally expandable material and a second binder, the second thermally expansive layer having a second ratio of the second thermally expandable material with respect to the second binder, wherein the second ratio is lower than the first ratio.
1. A thermally expandable sheet comprising:
a base;
a first thermally expansive layer formed on the base,
wherein the first thermally expansive layer comprises a first thermally expandable material and a first binder, and
wherein the first thermally expansive layer has a first ratio of the first thermally expandable material with respect to the first binder; and
a second thermally expansive layer formed on the first thermally expansive layer,
wherein the second thermally expansive layer comprises a second thermally expandable material and a second binder, and
wherein the second thermally expansive layer has a second ratio of the second thermally expandable material with respect to the second binder,
wherein the second ratio is lower than the first ratio.
2. The thermally expandable sheet according to claim 1 ,
wherein a thickness of the second thermally expansive layer is thinner than a thickness of the first thermally expansive layer.
3. The thermally expandable sheet according to claim 2 , further comprising:
an ink reception layer formed on the second thermally expansive layer,
wherein the ink reception layer is configured to receive ink.
4. The thermally expandable sheet according to claim 1 ,
wherein the first thermally expandable material and the second thermally expandable material are the same material.
5. The thermally expandable sheet according to claim 4 ,
wherein each of the first thermally expandable material and the second thermally expandable material comprises microcapsules,
wherein each of the microcapsules comprises a shell and a vaporizing substance in the shell, and
wherein a thickness of the second thermally expansive layer corresponds to a combined thickness of one to ten times the average particle size of the microcapsules.
6. The thermally expandable sheet according to claim 1 ,
wherein the second thermally expansive layer further comprises white pigment comprising one of titanium oxide, barium sulfate and zinc oxide.
7. The thermally expandable sheet according to claim 1 ,
wherein the first binder of the first thermally expansive layer and the second binder of the second thermally expansive layer are the same material.
8. The thermally expandable sheet according to claim 1 , further comprising:
a third thermally expansive layer provided between the base and the first thermally expansive layer,
wherein the third thermally expansive layer comprises a third thermally expandable material and a third binder,
wherein the third thermally expansive layer has a third ratio of the third thermally expandable material with respect to the third binder, and
wherein the third ratio is lower than the first ratio.
9. A thermally expandable sheet comprising:
a base;
a first thermally expansive layer formed on the base,
wherein the first thermally expansive layer comprises a first binder and a first thermally expandable material dispersed in the first binder at a first ratio; and
a second thermally expansive layer formed on the first thermally expansive layer,
wherein the second thermally expansive layer comprises a second binder and a second thermally expandable material dispersed in the second binder at a second ratio,
wherein the second ratio is lower than the first ratio.
10. The thermally expandable sheet according to claim 1 ,
wherein the first ratio is one of a volume ratio of the first thermally expandable material to the first binder, a weight ratio of the first thermally expandable material to the first binder, and a density of the first thermally expandable material contained in the first binder, and
wherein the second ratio is one of a volume ratio of the second thermally expandable material to the second binder, a weight ratio of the second thermally expandable material to the second binder, and a density of the second thermally expandable material contained in the second binder.