Nanofibrous materials for heavy metal adsorption
Water filtration membranes are provided. Such membranes include polysaccharide fibers that have been modified to possess thiol groups thereon, resulting in materials that effectively bind heavy metal ions. The resulting fibers may be used by themselves or applied to a scaffold to form a membrane suitable for removing heavy metals from water, including groundwater.
1. A method comprising:
contacting ultra-fine polysaccharide nanofibers with an oxidation agent, an acid, and a base, to form an activated polysaccharide nanofiber possessing functional groups selected from the group consisting of carboxylates, aldehydes, amines, and combinations thereof;
contacting the activated polysaccharide nanofiber with at least one reactant selected from the group consisting of cystamine, 3-amino-1-propanethiol, 6-amino-1-hexanethiol, 8-amino-1-octanethiol, 11-amino-1-undecanethiol, 16-amino-1-hexadecanethiol, 3-mercaptopropionic acid, 6-mercaptohexanoic acid, 8-mercaptooctanoic acid, 11-mercaptoundecanoic acid, 12-mercaptododecanoic acid, 16-mercaptohexadecanoic acid, and combinations thereof to form thiol-functional polysaccharide nanofibers; and
recovering the thiol-functional polysaccharide nanofibers possessing thiol groups.
2. The method of claim 1 , further comprising contacting the ultra-fine polysaccharide nanofibers, the at least one reactant, or both, with a catalyst.
3. The method of claim 2 , wherein the catalyst is selected from the group consisting of 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride, N-hydroxysuccinimide, and combinations thereof.
4. The method of claim 1 , wherein the ultra-fine polysaccharide nanofibers include a polysaccharide selected from the group consisting of cellulose, chitin, collagen, gelatin, chitosan, microcrystalline cellulose, bacterial cellulose, starch, alginic acid, and combinations thereof.
5. The method of claim 1 , wherein the oxidation agent is selected from the group consisting of sodium hypochlorite, sodium chlorite, concentrated nitric acid/sodium nitrite, and combinations thereof.
6. The method of claim 1 , wherein the acid is selected from the group consisting of hydrochloric acid, nitric acid, sulfuric acid, perchloric acid, trifluoroacetic acid, formic acid, and combinations thereof.
7. The method of claim 1 , wherein the base is selected from the group consisting of sodium hydroxide, lithium hydroxide, potassium hydroxide, and combinations thereof.
8. The method of claim 1 , further comprising forming a membrane with the thiol-functional polysaccharide nanofibers.
9. The method of claim 8 , further comprising contacting a nanofibrous scaffold layer with a solution possessing the thiol-functional polysaccharide nanofibers.
10. The method of claim 9 , wherein the scaffold layer comprises nanofibers having diameters from about 50 nm to about 500 nm.
11. The method of claim 9 , wherein the scaffold layer possesses pores with average pore sizes from about 10 nm to about 200 μm.
12. The method of claim 9 , wherein the scaffold layer has a thickness of from about 10 μm to about 300 μm.
13. The method of claim 9 , further comprising applying the nanofibrous scaffold to a substrate layer comprising non-woven fibers of a material selected from the group consisting of poly(ethylene terephthalate), polypropylene, glass and cellulose.