Aluminum alloy slug for impact extrusion
Novel recycled aluminum alloys are provided for use in an impact extrusion manufacturing process to create shaped containers and other articles of manufacture. In one embodiment blends of recycled scrap aluminum are used in conjunction with relatively pure aluminum to create novel compositions which may be formed and shaped in an environmentally friendly process. Other embodiments include methods for manufacturing a slug material comprising recycled aluminum for use in the impact extraction process.
1. An aluminum alloy used in a slug for an impact extrusion process to form a metallic container having an upper end with an opening configured to receive an end closure, the aluminum alloy formed from a combination of:
between 40 wt. % and 90 wt. % of one of a 1070 aluminum alloy and a 1050 aluminum alloy; and
between 10 to 60 wt. % of one of a 3105, a 3004, a 3003, a 3103, a 3013 and a 3104 aluminum alloy, and
wherein a composition of the aluminum alloy, comprises:
at least 97.84 wt. % Al and no more than 99.31 wt. % Al;
at least 0.10 wt. % Si and no more than 0.38 wt. % Si;
at least 0.25 wt. % Fe and no more than 0.5 wt. % Fe;
at least 0.05 wt. % Cu and no more than 0.19 wt. % Cu;
at least 0.07 wt. % Mn and no more than 0.61 wt. % Mn;
at least 0.05 wt. % Mg and no more than 0.73 wt. % Mg;
at least 0.03 wt. % Zn and no more than 0.25 wt. % Zn;
at least 0.02 wt. % Cr and no more than 0.13 wt. % Cr;
about 0.01 wt. % Ti; and
the balance in impurities.
2. The aluminum alloy of claim 1 , wherein the aluminum alloy is blended from the 1070 alloy, and the 3104 alloy.
3. The aluminum alloy of claim 1 , wherein the aluminum alloy is blended from 60-80 wt. % of the 1070 alloy and the balance of the 3104 aluminum alloy.
4. The aluminum alloy of claim 1 , wherein the aluminum alloy consists of:
between 97.84 and 99.08 wt. % aluminum;
between 0.10 and 0.2 wt. % Si;
between 0.25 and 0.38 wt. % Fe;
between 0.05 and 0.13 wt. % Cu;
between 0.21 and 0.61 wt. % Mn; and
between 0.25 and 0.73 wt. % Mg.
5. The aluminum alloy of claim 1 , comprising:
between 98.22 wt. % and 99.2 wt. % Al;
between 0.16 wt. % and 0.38 wt. % Si;
between 0.29 wt. % and 0.50 wt. % Fe;
between 0.07 wt. % and 0.19 wt. % Mn; and
between 0.05 wt. % and 0.13 wt. % Mg.
6. The aluminum alloy of claim 1 , wherein the slug used in the impact extrusion process is formed by melting the one of the 1070 aluminum alloy and the 1050 aluminum alloy, and between 10 to 60 wt. % of the one of the 3105, the 3004, the 3003, the 3103, the 3013 and the 3104 aluminum alloy in an indirect heating process to reduce surface oxidation of said aluminum alloy.
7. The aluminum alloy of claim 1 , further comprising a titanium boride.
8. The aluminum alloy of claim 7 , wherein a concentration of the titanium boride is between about 0.5 to 1.3 kg per metric ton.