Systems and methods for creating nanocrystalline alloy articles using additive manufacturing
Embodiments described herein relate generally to systems and methods for using nanocrystalline metal alloy particles or powders to create nanocrystalline and/or microcrystalline metal alloy articles using additive manufacturing. In some embodiments, a manufacturing method for creating articles includes disposing a plurality of nanocrystalline particles and selectively binding the particles together to form the article. In some embodiments, the nanocrystalline particles can be sintered to bind the particles together. In some embodiments, the plurality of nanocrystalline particles can be disposed on a substrate and sintered to form the article. The substrate can be a base or a prior layer of bound particles. In some embodiments, the nanocrystalline particles can be selectively bound together (e.g., sintered) at substantially the same time as they are disposed on the substrate.
1. A method of manufacturing a metal alloy article, comprising:
disposing a plurality of nanocrystalline metal particles and a binder, the nanocrystalline metal particles having an average particle size of greater than about 1 μm;
selectively binding the nanocrystalline metal particles together to form a green body;
vaporizing the binder at a first temperature; and
sintering the green body at a second temperature such that the nanocrystalline metal particles remain solid throughout the sintering to form the metal alloy article,
wherein the second temperature is different than the first temperature.
2. The method of claim 1 , wherein the nanocrystalline metal particles are disposed onto a substrate.
3. The method of claim 1 , wherein the nanocrystalline metal particles are disposed using an additive manufacturing process.
4. The method of claim 3 , wherein the nanocrystalline metal particles are disposed on at least one of a substrate and at least a portion of a prior layer from the additive manufacturing process.
5. A method of manufacturing a metal alloy article, comprising:
combining a plurality of nanocrystalline particles and a binder to create an intermediate material, the nanocrystalline particles having an average particle size of greater than about 1 μm;
selectively causing the binder to bind such that a connected network of intermediate material is formed;
vaporizing the binder at a volatilization temperature; and
sintering the connected network of intermediate material at a sintering temperature such that the nanocrystalline particles remain solid throughout the sintering to form the metal alloy article,
wherein the sintering temperature is different than the volatilization temperature.
6. The method of claim 5 , wherein the connected network is a green body.
7. The method of claim 6 , wherein the green body is sintered to form the article.
8. The method of claim 5 , wherein the plurality of nanocrystalline particles include a first plurality of nanocrystalline particles comprising a first metal material and a second plurality of nanocrystalline particles comprising a second metal material.
9. The method claim 5 , wherein the binder includes a wax.
10. A method of manufacturing a metal alloy article, comprising:
disposing a plurality of nanocrystalline particles, the nanocrystalline particles including a first metal material and a second metal material and having an average particle size of greater than about 1 μm, and a binder;
selectively binding the nanocrystalline particles and/or the binder;
vaporizing the binder; and
after the binder is substantially vaporized, sintering the nanocrystalline particles at a sintering temperature such that the first metal material and the second metal material remain solid throughout the sintering to form the metal alloy article.
11. The method of claim 10 , wherein selectively binding the nanocrystalline particles and/or the binder forms a green body.
12. A method of manufacturing a metal alloy article, comprising:
disposing a plurality of nanocrystalline particles and a binder, the nanocrystalline particles having an average particle size of greater than about 1 μm;
selectively binding the nanocrystalline particles and/or the binder;
vaporizing the binder at a first temperature; and
sintering the nanocrystalline particles at a second temperature such that the nanocrystalline particles remain solid throughout the sintering to form the metal alloy article,
wherein the second temperature is different than the first temperature.
13. The method of claim 12 , wherein the first temperature is less than the second temperature.
14. The method of claim 12 , wherein the nanocrystalline particles are coated with the binder.
15. The method of claim 1 , wherein the plurality of nanocrystalline metal particles include a first plurality of nanocrystalline particles comprising a first metal material, and a second plurality of nanocrystalline particles comprising a second metal material.
16. The method of claim 10 , wherein selectively binding the nanocrystalline particles and/or the binder includes a chemical fusion process.
17. The method of claim 12 , wherein the plurality of nanocrystalline particles include a first plurality of nanocrystalline particles comprising a first metal material, and a second plurality of nanocrystalline particles comprising a second metal material.
18. The method claim 5 , wherein the binder includes a polymer.
19. The method claim 5 , wherein the binder includes a metal.