Advanced high temperature environmental barrier coating for SiC/SiC ceramic matrix composites
Advanced environmental barrier coating bond coat systems with higher temperature capabilities and environmental resistance are disclosed. These bond coat systems can be applied to ceramic substrates such as SiC/SiC ceramic matrix composite substrates, and can provide protection from extreme temperature, mechanical loading and environmental conditions, such as in high temperature gas turbines. Example bond coat systems can include either an advanced silicon/silicide component, an oxide/silicate component, or a combination thereof.
1. An environmental barrier coating system disposed on a substrate, the coating system comprising:
a bond coat layer disposed on the substrate, the bond coat layer comprising a rare earth (RE) silicon component and a silicate oxide component, wherein:
the rare earth (RE) silicon component is selected from:
a RE silicon alloy,
a RE silicide,
a RE doped refractory transition metal silicide,
a RE and aluminum doped palladium, iridium, or platinum silicide,
a RE tantalum-, titanium-, chromium-, molybdenum-, niobium-, aluminum-, silicon, carbon, boron, nitride compounds with silicon,
one of Ti x (AlCrTa) y Si—CN, Ti x (AlCrTa) y Si—BN, Ti 2 CrTa(Si)—N, ZrTaSi—N, HfTaSiCN, and Ta 2 AlSi—CN, and
a combination of two or more thereof,
the silicate oxide component is doped or alloyed with ZrO 2 or HfO 2 , wherein the silicate oxide component is selected from a RE mono-silicate, a RE di-silicate, or a combination thereof;
a first environmental barrier coating (EBC) disposed on the bond coat layer, wherein the first EBC comprises a rare earth aluminosilicate compound or composite comprising a rare earth silicate composition and an alumina dopant; and
a second EBC disposed on the first EBC, wherein the second EBC possesses a graded columnar structure comprising a HfO 2 or ZrO 2 -based ceramic alloy doped with SiO 2 and a RE oxide, wherein a concentration of the SiO 2 dopant decreases with distance from the substrate, wherein a concentration of the RE oxide dopant increases with distance from the substrate.
2. The environmental barrier coating system of claim 1 , wherein the rare earth silicate composition is selected from a rare earth monosilicate, a rare earth disilicate, or a rare earth oxide-silicate.
3. The environmental barrier coating system of claim 2 , wherein the rare earth silicate composition is selected from Yb 2 SiO 5 , Yb 2 Si 2 O 7 , Gd 2 SiO 5 , Gd 2 Si 2 O 7 , Y 2 SiO 5 , or Y 2 Si 2 O 7 .
4. The environmental barrier coating system of claim 1 , wherein the rare earth silicate composition of the barrier layer is co-doped with t′HfO 2 , t′ZrO 2 , or t′HfO 2 —ZrO 2 .
5. The environmental barrier coating system of claim 1 , wherein the rare earth aluminosilicate compound or composite is a rare earth aluminumgarnet silicate, a rare earth aluminum monoclinic silicate, or a rare earth aluminumperovskite silicate.
6. The environmental barrier coating system of claim 5 , wherein the rare earth aluminum compound is selected from SiO 2 containing Yb 3 Al 5 O 12 , YbAG, GdAG, YAM, YbAM, YAP, or YbAP.
7. The environmental barrier coating system of claim 1 , wherein the alumina dopant is present in the first EBC in an amount in the range of about 2 mol % to about 20 mol %.
8. The environmental barrier coating system of claim 1 wherein the RE silicon component is the rare earth silicide, wherein the rare earth silicide is selected from the group consisting of ytterbium silicides, yttrium silicides, gadolinium silicides, erbium silicides, or a combination of two or more thereof.
9. The environmental coating system of claim 1 , wherein the second EBC is doped with alumina, wherein alumina is present in the second EBC in an amount in the range of about 2 to about 20 mol %.
10. The environmental barrier coating system of claim 1 , wherein the bond coat layer comprises a silicon concentration from about 50 to about 70 mol %.
11. The environmental barrier coating system of claim 1 , wherein the bond coat layer comprises a rare earth silicide co-doped and co-alloyed with at least one of hafnium oxide or zirconium oxide, wherein the amount of hafnium oxide or zirconium oxide is in the range of about 2 to about 20 mol %.