Method for manufacturing self-healing hydrogel-filled separation membrane for water treatment
A method for manufacturing a self-healing hydrogel-filled separation membrane for water treatment includes soaking a porous support comprising pores in a monomer solution to fill the pores with the solution, removing the excessively filled monomer solution from the porous support, and forming a hydrogel in the pores by crosslinking the monomer. The separation membrane does not require an additional repair process when damage occurs to the separation membrane and can exhibit superior self-healing effect and physical stability.
1. A method for manufacturing a self-healing separation membrane for water treatment, the method comprising:
soaking a porous support having pores in a monomer solution to fill the pores with the monomer solution;
removing an excessively filled monomer solution from the porous support; and
forming a hydrogel in the pores by irradiating UV to the filled monomer solution without a photoinitiator to form a covalent bonding between the porous support and monomers of the filled monomer solution and polymerize the monomers through graft polymerization,
wherein the porous support is formed of a polymer selected from the group consisting of polyethersulfone and polysulfone;
the monomer solution comprises at least 20 wt % of the monomers; and
the monomers are at least one selected from the group consisting of acrylamidoxime, N-acryloyl tris(hydroxymethyl)methylamine, N,N-diethylacrylamide, N,N-dimethylacrylamide, 2-(N,N-dimethylamino)ethyl acrylate, 2-(N,N-dimethylamino)ethyl methacrylate, N-[3-(N,N-dimethylamino)propyl]methacrylamide, dodecyl methacrylamide, N-(hydroxymethyl)acrylamide, N-methacryloylacrylamide, octylacrylamide, acrylamido-2-methyl-1-propanesulfonic acid (AMPS), and (3-acrylamidopropyl) trimethyl ammonium chloride (APTAC).
2. The method according to claim 1 , wherein the excessively filled monomer solution is removed by compressing the porous support.
3. The method according to claim 1 , wherein the monomer solution comprises 20 to 50 wt % of the monomers.
4. The method according to claim 1 , wherein the pores have an average size of 0.01 μm to 10 μm.
5. The method according to claim 1 , further comprising washing away an unreacted monomer after the hydrogel is formed in the pores.
6. The method according to claim 1 , wherein the hydrogel is formed in the pores as the monomers are polymerized by irradiating UV with an intensity of 100 to 1,000 μW/cm 2 for 30 to 60 minutes, which induce the covalent bonding between the porous support and the monomers, and the polymerization of the monomers through the graft polymerization.
7. The method according to claim 1 , wherein the monomers are at least one selected from the group consisting of acrylamidoxime, 2-(N,N-dimethylamino)ethyl acrylate, 2-(N,N-dimethylamino)ethyl methacrylate, acrylamido-2-methyl-1-propanesulfonic acid (AMPS), and (3-acrylamidopropyl) trimethyl ammonium chloride (APTAC).
8. The method according to claim 1 , wherein the monomers are at least one selected from the group consisting of acrylamidoxime, 2-(N,N-dimethylamino)ethyl acrylate, 2-(N,N-dimethylamino)ethyl methacrylate, and (3-acrylamidopropyl) trimethyl ammonium chloride (APTAC).
9. The method according to claim 1 , wherein the monomers are acrylamido-2-methyl-1-propanesulfonic acid (AMPS).
10. The method according to claim 1 , wherein the monomer solution comprises 20 to 50 wt % of the monomers; and
the pores have an average size of 0.01 μm to 10 μm.